Investigation of Dielectric Properties of Polyethylene Terephthalate under Different Aging Temperatures

Wenxia Sima,Xiongwei Jiang,Qingjun Peng,Potao Sun

DOI: https://doi.org/10.1109/tdei.2017.006490

IF: 2.509

2017-01-01

IEEE Transactions on Dielectrics and Electrical Insulation

Abstract:The polyethylene terephthalate (PET) is widely used in dry-type insulation application because of its excellent insulation properties. In practice, thermal aging of PET is often encountered, but the related mechanisms and effect of thermal aging on the PET dielectric properties still remain unclear. In the present paper, we presented a systematic and comparative study on the effect of thermal aging on surface microscopic morphological characteristics, DC breakdown strength, trap depths and the apparent mobility. The results indicate that when aged at 130 degrees C, the surface topography becomes coarser than that aged at 80 degrees C. The polarity reversal at the PET/PET interface during the polarization indicates that the injection abilities of Al and Sc electrodes are gradually enhanced when aged at 80 degrees C and 130 degrees C, respectively. Moreover, the measured isothermal discharge currents during depolarization show that the trap depth corresponding to the maximum trap density increases significantly in the beginning of aging, and then it decreases gradually when aged at 80 degrees C, but it increases evidently when aged at 130 degrees C with increasing the aging degree. It also has been found that the apparent trap-controlled charge mobility is greatly enhanced when aged at 80 degrees C with the increase in thermal aging degree. This enhancement is proved to be associated with the decrease in trap energy level at the PET/PET interface. Also, it can be preliminary concluded that the enhancement of DC breakdown strength (at 1500 h) is closely related to the increase in electron type trap energy and its density when aged at 130 degrees C.