Abstract:Porous alumina has been widely used as catalytic support for industrial processes. Under carbon emission constraints, developing a low-carbon porous aluminum oxide synthesis method is a long-standing challenge for low-carbon technology. Herein, we report a method involving the only use of elements of the aluminum-containing reactants (e.g. sodium aluminate and aluminum chloride), sodium chloride was introduced as the coagulation electrolyte to adjust the precipitation process. Noticeably, the adjustment of the dosages of NaCl would allow us to tailor the textural properties and surface acidity with a volcanic-type change of the assembled alumina coiled plates. As a result, porous alumina with a specific surface area of 412 m<sup>2</sup>/g, large pore volume of 1.96 cm<sup>3</sup>/g, and concentrated pore size distribution at 30 nm was obtained. The function of salt on boehmite colloidal nanoparticles was proven by colloid model calculation, dynamic light scattering, and scanning/transmission electron microscopy. Afterward, the synthesized alumina was loaded with PtSn to prepare catalysts for the propane dehydrogenation reaction. The obtained catalysts were active but showed different deactivation behavior that was related to the coke resistance capability of the support. We figure out the correlation between pore structure and the activity of the PtSn catalysts associated with the maximum conversion of 53 % and minimum deactivation constant occurring at the pore diameter around 30 nm of the porous alumina. This work offers new insight into the synthesis of porous alumina.

Morphology-controlled fabrication of biomorphic alumina-based hierarchical LDH compounds for propane dehydrogenation reaction

Hierarchical MgAl2O4 Supported Pt-Sn As a Highly Thermostable Catalyst for Propane Dehydrogenation

Ph-Dependent Growth of Alumina Nanorods with a High Aspect Ratio for Enhanced Propane Dehydrogenation Performance

The Effect of Catalytic Structure-modification on Hydrogenolysis of Glycerol into 1,3-propanediol over Platinum Nanoparticles and Ordered Mesoporous Alumina Assembled Catalysts

Peony-like Pentahedral Al(III)-Enriched Alumina Nanosheets for the Dehydrogenation of Propane

Salt-assisted surface charge driven synthesis of large pores alumina as carbon tolerance support for propane dehydrogenation

Construction of Highly Stable and Efficient Zn-based Catalyst Via Mg Modification for Propane Dehydrogenation

Tailoring Pd/M@CoAlO Core-Shell Catalyst Morphology for Efficient Methane Oxidation

Synthesis of Magnesium-Modified Mesoporous Al2O3 with Enhanced Catalytic Performance for Propane Dehydrogenation

From Nano-to Macro-Engineering of LDHs-derived Nanocomposite Catalysts for Harsh Reactions

Structure Evolution of Porous Alumina During Aging Process and Its Support Effect on Ptsn/Al2o3 Catalyzed Propane Dehydrogenation

Optimizing propylene selectivity and stability over Pt–Sn/MgAl2O4 catalysts for propane dehydrogenation

Biomolecule-inspired synthesis of framework zinc in MFI zeolite for propane dehydrogenation

Preparation of carbon-doped alumina beads and their application as the supports of Pt–Sn–K catalysts for the dehydrogenation of propane

Influence of Alumina Content on Catalytic Performance of Ptsn/Al2o3/Sba-15 Catalysts for Propane Dehydrogenation

In-Situ Co-Precipitation of Ni-Mg-Al-Ldh Catalytic Precursor on Y-Al2o3 for Dry Reforming of Methane: Synthesis and Evaluation

The Acid Roles of PtSn@Al2O3 in the Synthesis and Performance of Propane Dehydrogenation

A novel Ni–Mg–Al-LDHs/γ-Al 2 O 3 Catalyst Prepared by in-situ synthesis method for CO 2 reforming of CH 4

Rod-shaped Porous Alumina-Supported Cr2O3 Catalyst with Low Acidity for Propane Dehydrogenation

In Situ Fabrication of the Al2O3@NiMo Core-Shell Catalyst from LDH for Low-Pressure Hydrodeoxygenation of Fatty Acid Methyl Ester

Synthesis of Hierarchically Structured Alumina Support with Adjustable Nanocrystalline Aggregation Towards Efficient Hydrodesulfurization