Heterogeneous Fenton-like catalysis of Fe-MOF derived magnetic carbon nanocomposites for degradation of 4-nitrophenol

Dezhi Chen,Shasha Chen,Yijie Jiang,Shasha Xie,Hongying Quan,Li Hua,Xubiao Luo,Lin Guo
DOI: https://doi.org/10.1039/c7ra09234b
IF: 4.036
2017-01-01
RSC Advances
Abstract:Magnetic carbon nanocomposites (Fe-C-x) as heterogeneous Fenton-like catalysts were synthesized by the pyrolysis of iron based metal-organic frameworks (Fe-MOF), and the degradation removal of 4-nitrophenol (4-NP) in aqueous solution was used to evaluate the catalytic activity of Fe-C-x. The results showed that 4-NP could be effectively degraded by Fe-C-x in the presence of hydrogen peroxide. Pyrolysis temperature significantly affected the component, structures and performances of the catalysts, and the as-prepared Fe-C-500 exhibited the best catalytic performance. Furthermore, the effects of several reaction conditions, such as catalyst loading, H2O2 dosage, reaction temperature, and initial pH, on the catalytic degradation of 4-NP were extensively analyzed for the practical applications of Fe-C-500. At an initial circumneutral pH of 6.21, 89.0% of 0.36 mM 250 mL of 4-NP solution could be degradated after 75 min by the heterogeneous Fenton-like oxidation on the 0.08 g L-1 of Fe-C-500 in the presence of 7.8 mM H2O2. The results of activation energy and the reaction kinetics showed Fe-C-500 possessed a high catalytic activity in the heterogeneous Fenton reaction of 4-NP. Moreover, the prepared Fe-C-500 could be reused by an external magnet, and still retained good catalytic activity with 52.4% degradation of 4-NP at the fourth cycle.
What problem does this paper attempt to address?