Abstract:Poly(vinyl alcohol-co-ethylene) (EVOH) nanofibrous aerogel (NFA) templates were fabricated through vacuum freeze-drying from EVOH nanofibrous suspensions. Aluminum oxide (Al2O3) layers were deposited onto highly porous templates to form organic–inorganic hybrid aerogels by the atomic layer deposition (ALD) technique. Chemical and physical measurements showed that mechanical properties were improved through ALD. In addition, the surface chemistry of ALD modified aerogels showed a fascinating cyclic change based on the number of ALD deposition cycles. A transition from hydrophilicity to hydrophobicity was observed after a few cycles of ALD coating; however, additional deposition cycles changed the wettability characteristics back to hydrophilicity. This hydrophilic–hydrophobic–hydrophilic variation is shown to be governed by a combination of geometrical and chemical surface properties. Furthermore, the deposited Al2O3 could substantially improve aerogels strength and reduce permanent deformation after cyclic compression. The Young's modulus of aerogels increased from 5.54 to 33.27 kPa, and the maximum stress at 80% strain went up from 31.13 to 176.11 kPa, after 100 cycles of trimethyl-aluminum (TMA)/water ALD. Thermogravimetric analysis (TGA) results confirm that ALD can effectively improve the heat resistance characteristics of polymeric aerogel. The onset temperature and the residual mass increased with increasing numbers of ALD cycles. During pyrolysis, the nanofiber cores were decomposed, and the brittle pure Al2O3 self-supporting nanotube aerogels with the continuous hollow nanotubular network were formed. A coating of continuous thickness Al2O3 layer on individual nanofiber was achieved after 100 ALD cycles. In additional to mechanical strength and physical property changes, the ALD modified aerogel also shows a superhydrophobic and oleophilic surface chemistry, which could potentially be used to remove oils/organic solvents from water. The resultant aerogels exhibit excellent absorption capacity (31–73 g/g) for various liquids, and the material could be reused after distillation or squeezing. A successful scale-up of such materials could provide some insights into the design and development of thermoplastic polymeric NFAs with substantial industrial applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.9b09497?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.9b09497</a>.Figures S1–S18 and Tables S1–S5 showing reaction mechanisms, SEM images, AFM images, XPS spectrum, mechanisms of cross-linking and esterification, dynamic water contact angles, wicking properties, photographs of water absorption, cyclic stress–strain curves, TEM images, onset temperature of weight loss stages, thickness of Al2O3 coatings, physical properties, surface average roughness variations, peak BE and atomic ratio of various aerogels, comparison of sorption capacities (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.9b09497/suppl_file/nn9b09497_si_001.pdf">PDF</a>)Movie S1: Dynamic compressive behavior of 6cy-ALD aerogels under a 60% compressive strain (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.9b09497/suppl_file/nn9b09497_si_002.avi">AVI</a>)Movie S2: Canola oil absorbed by 6cy-ALD aerogels (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.9b09497/suppl_file/nn9b09497_si_003.avi">AVI</a>)Movie S3: Chloroform absorbed by 6cy-ALD aerogels (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.9b09497/suppl_file/nn9b09497_si_004.avi">AVI</a>)This article has not yet been cited by other publications.

Ultralight And Resilient Al2o3 Nanotube Aerogels With Low Thermal Conductivity

Ultralight ZrB 2 /ZrC nanofiber aerogels with excellent elasticity and ultra-low thermal conductivity

Ultralight elastic Al2O3 nanorod-graphene aerogel for pressure sensing and thermal superinsulation

Facile and Green Strategy for Designing Ultralight, Flexible, and Multifunctional PVA Nanofiber‐Based Aerogels

Gradient All-Nanostructured Aerogel Fibers for Enhanced Thermal Insulation and Mechanical Properties

Ultralight and Superelastic Curly Micro/Nanofibrous Aerogels by Direct Electrospinning Enable High‐Performance Warmth Retention

Ultralight, thermal insulating, and high-temperature-resistant mullite-based nanofibrous aerogels

A lightweight and high compressive resistance thermal insulation material with dual-network structure

Transparent, Ultraflexible, and Superinsulating Nanofibrous Biocomposite Aerogels Via Ambient Pressure Drying

Ultralight nanofibre-assembled cellular aerogels with superelasticity and multifunctionality

Ultralight Multiwalled Carbon Nanotube Aerogel.

Ultrastrong, Superelastic, and Lamellar Multiarch Structured ZrO 2 –Al 2 O 3 Nanofibrous Aerogels with High-Temperature Resistance over 1300 °C

Three-Dimensional Reticulated, Spongelike, Resilient Aerogels Assembled by SiC/Si3N4 Nanowires

Ultralight aerogel textiles based on aramid nanofibers composites with excellent thermal insulation and electromagnetic shielding properties

Facile Preparation of Carbon Nanotube Aerogels with Controlled Hierarchical Microstructures and Versatile Performance

Atomic Layer Deposition onto Thermoplastic Polymeric Nanofibrous Aerogel Templates for Tailored Surface Properties

Ultra-Light and Ultra-Low Thermal Conductivity of Elastic Silica Nanofibrous Aerogel with TiO2 Opacifier Particles as Filler

Ambient-drying to construct unidirectional cellulose nanofibers/ carbon nanotubes aerogel with ultra-lightweight, robust, and superior microwave absorption performance

Lightweight carbon nanotube/aramid nanofiber aerogel with superior electromagnetic wave absorption, thermal insulation, and flame resistance

Nanofibrous Aerogel Bulk Assembled by Crosslinked SiC/SiOx Core-Shell Nanofibers with Multifunctionality and Temperature-Invariant Hyperelasticity.

Ionic Liquid Directed Spinning of Cellulose Aerogel Fibers with Superb Toughness for Weaved Thermal Insulation and Transient Impact Protection