Preparing High-Efficiency Perovskite Solar Cells
Qingfeng Dong,Zhengguo Xiao,Qi Wang,Cheng Bi,Yuchuan Shao,Jinsong Huang
DOI: https://doi.org/10.1117/2.1201407.005529
2014-01-01
SPIE Newsroom
Abstract:Organometal trihalide perovskites are emerging as a new generation of photovoltaic materials. They are abundant in nature and have rapidly increasing power conversion efficiencies (PCE) of above 15% in common hybrid (mixed organic/inorganic) thin-film-based solar cells.1–3 Up to now, perovskite films have been formed by film deposition approaches such as spin-coating, sequential deposition of the inorganic and organic precursor, and co-evaporation of the precursors.1, 2 Low-temperature solution processes are among the simplest ways to fabricate planar low-cost photovoltaic devices. However, perovskite crystallizes very rapidly, so it is very challenging to form uniform, continuous, and leakage-free perovskite films by solution methods.2 We developed two simple and effective low-temperature solution processes to fabricate high-efficiency perovskite devices (see Figure 1). In the first approach, we studied the influence of the ratio of the precursors methylammonium iodide (CH3NH3I) and lead iodide (PbI2) in a premixed solution. 3 We found that using a non-stoichiometric precursor solution (i.e., not in a simple ratio) was critical to forming stoichiometric (i.e., in a simple ratio) perovskite films. The compositions of the spun perovskite films were very sensitive to the substrate surface, and could be very different from those of the precursor solutions. We varied the composition of the precursor solution, and found a PbI2/CH3NH3Xmolar ratio of 0.6–0.7 gave the best surfacemorphology and electronic properties, such as doping concentration. We used a planar heterojunction device structure of ITO/ PEDOT:PSS/(CH3NH3I)/PCBMor ICBA/C60/BCP/aluminum, where ITO is a substrate of indium tin oxide, PEDOT:PSS is an electron-donating transparent conductive polymer, PCBM and ICBA are fullerene-derived electron acceptors, C60 is buckminsterfullerene (a spherical fullerene molecule), and BCP is 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline, an electrontransporting but hole-blocking layer. Figure 1. Schematic of the prepation of perovskite films by (a) spin coating of pre-mixed precursor of lead iodide (PbI2) and methylammonium iodide (CH3NH3I) and (b) an interdiffusion approach. ITO: Indium tin oxide, a transparent conducting oxide. PEDOT:PSS: A transparent, conductive polymer. MAI: Methylammonium iodide. MAPbI3 Methylammonium lead iodide.