Hydrogen Storage and Electrochemical Properties of Pr, Nd and Co-free La13.9Sm24.7Mg1.5Ni58Al1.7Zr0.14Ag0.07 Alloy As a Nickel-Metal Hydride Battery Electrode

Liuzhang Ouyang,Tonghan Yang,Min Zhu,De Min,Tongzhao Luo,Hui Wang,Fangming Xiao,Renheng Tang

DOI: https://doi.org/10.1016/j.jallcom.2017.10.268

IF: 6.2

2017-01-01

Journal of Alloys and Compounds

Abstract:A Pr, Nd and Co-free A(2)B(7)-type alloy, La13.9Sm24.7Mg1.5Ni58Al1.7Zr0.14Ag0.07, was prepared for use as a nickel-metal hydride battery electrode. The structural characteristics and hydrogen-storage and electrochemical properties of La13.9Sm24.7Mg1.5Ni58Al1.7Zr0.14Ag0.07 were investigated in detail. The La13.9Sm24.7Mg1.5Ni58Al1.7Zr0.14Ag0.07 alloy consisted of two phases (La2Ni7 and LaNi5) and showed excellent hydrogen-storage and electrochemical performance. The Delta H and Delta S values of this alloy were 24.4 kJ/mol H-2 and 66.2 J/(mol.K), respectively. The high rate dischargeabilities were 97%, 86% and 78%, respectively, at discharge current densities of 330, 970 and 1600 mAh/g. The hydrogen desorption pressure of the La13.9Sm24.7Mg1.5Ni58Al1.7Zr0.14Ag0.07 alloy was 0.005 MPa at 233 K, which is favour for the low temperature discharging. The retention rate maintained a high value of 86.2% after 200 cycles at 1 C. (C) 2017 Elsevier B.V. All rights reserved.