High Temperature Characterization and Evolution of Delamination Crack in Thermal Barrier Coating
Zheng Wei,Congyang Zhang,Changbo Liu,Hui Dong,Xiaotao Luo,Yuan Deng,Changjiu Li
DOI: https://doi.org/10.11933/j.issn.1007-9289.20220926001
2020-01-01
China surface engineering
Abstract:Air-plasma-sprayed(APS) thermal barrier coatings(TBCs) are widely used for heat insulation in gas turbines. As reported by many studies in this field, the lifetime of as-sprayed coatings is one of the most concerning issues. The failure of the coatings is related to the formation and propagation of internal cracks. Effective nondestructive methods for characterizing and measuring the defects inside the coating may help establish theories for predicting the service life of TBCs, which are in great demand. However, current testing methods for detecting such defects are limited by the specimen and test environment requirements. The thermal resistance of the crack area perpendicular to the coating increases significantly because of the air in the debonding crack after the ceramic layer of the thermal barrier coating is locally delaminated with the metallic bond coat. According to our previous study, high thermal resistance in the vertical direction of the delamination crack area generated an increased local temperature on the corresponding surface of the ceramic layer and formed bright spots. In this study, we propose heating the ceramic layer surface of the thermal barrier coating with a flame and tracking the debonding defects by the bright spots on the coating surface. The experimental procedure is divided into three steps. First, by preparing salt spots on top of the bond coatings using flame spraying(FS) and resolving them in a water bath after spraying the ceramic layer, an effective method for internal defect prefabrication was established. Second, artificial defects between the ceramic and metallic bond coats of different sizes were fabricated through the FS process and observed using thermal imaging equipment to determine the lower limit of the debonding crack size observable based on the bright spot method. Finally, the evolution of the artificial debonding defects in a gradient thermal shock cycle was investigated. The results show that artificial delamination crack defects with specific shapes and sizes can be prefabricated at the interface between the YSZ and metal bonding layer by preparing water-soluble salt spots at the metallic-bond coating interface, flame-spraying through a mask, preparing the ceramic layer, and dissolving the salt spots with water. It was found that the surface bright spot size was linearly and positively correlated to the delamination crack size, with a slope of approximately 1.031. When the diameter of the preformed crack exceeded 0.4 mm, bright spots were observed on the coating surface. When the diameter of the preformed crack exceeded 0.7 mm, the relative error of predicting the crack size based on the bright spot size was less than 15%. Under gradient thermal shock cycling, with an increase in thermal shock time, the surface of the thermal barrier coating with a specific thermal growth oxide layer thickness first appeared as bright spots, and the bright spots grew and merged. After approximately 2 500 thermal cycles, the merging speed increased, and finally, the ceramic layer locally peeled off at the bright spots. Based on the blocking effect of debonding cracks on the longitudinal heat flow, a prefabrication method for artificial debonding crack defects was proposed, and the corresponding relationship between the size of the bright spot on the surface and the size of the internal debonding crack defect was established. Based on the evolution of the size and shape of the bright spots on the surface, the propagation and merging behaviors of the debonding crack were revealed. An effective, nondestructive method for examining the details of internal cracks inside TBCs is established, which can fill the space for nondestructive testing of TBCs and help establish theories regarding TBC lifetimes.