Hierarchically Structured NiFeOx/CuO Nanosheets/Nanowires As an Efficient Electrocatalyst for the Oxygen Evolution Reaction

Steffen Czioska,Jianying Wang,Shangshang Zuo,Xue Teng,Zuofeng Chen

DOI: https://doi.org/10.1002/cctc.201701441

IF: 4.5

2018-01-01

ChemCatChem

Abstract:It is desirable to fabricate hierarchically structured NiFe-based materials to further boost the performance of these state-of-the-art electrocatalysts for the oxygen evolution reaction (OER). Most of the NiFeOx catalysts in the form of layered double hydroxides feature a nanosheet structure, which limits their spatial extension at the electrode substrate. Herein, we report the fabrication of unique NiFeOx/CuO nanosheets/nanowires and their use as efficient electrocatalysts for the OER. The surface-bound Cu(OH)(2) nanowires were grown insitu on a copper substrate by a simple solution-based method, which were then converted to CuO nanowires by calcination in air. The coating of NiFeOx nanosheets was achieved by anodic co-deposition in concentrated carbonate solution containing Ni-II and Fe-III. The presence of concentrated carbonate anions allows Fe-III to be dissolved in a basic solution by complex ion formation. This strategy therefore avoids the destruction of CuO nanowires caused by the usual cathodic procedure in acidic solutions. At a planar copper foil, a small Tafel slope of 36mVdec(-1) was obtained in 1m KOH and a current density of 100mAcm(-2) was reached at a very low overpotential of 300mV from the Tafel plot. Electrolysis experiments showed high stability of the catalyst with nearly no loss in efficiency and morphology change after a prolonged period. The same catalyst could be established on a three-dimensional copper foam.