Mechanochemical redox-based synthesis of highly porous Co Mn1-O catalysts for total oxidation
Jiafeng Bao,Hao Chen,Shize Yang,Pengfei Zhang
DOI: https://doi.org/10.1016/s1872-2067(20)63635-x
IF: 16.5
2020-12-01
Chinese Journal of Catalysis
Abstract:A mechanochemical redox reaction between KMnO4 and CoCl2 was developed to obtain a Co x Mn1–x O y catalyst with a specific surface area of 479 m2 g−1, which was higher than that obtained using a co-precipitation (CP) method (34 m2 g−1), sol-gel (SG) method (72 m2 g−1), or solution redox process (131 m2 g−1). During catalytic combustion, this Co x Mn1–x O y catalyst exhibited better activity (T100 for propylene = ~200 °C) than the control catalysts obtained using the SG (325 °C) or CP (450 °C) methods. The mechanical action, mainly in the form of kinetic energy and frictional heating, may generate a high degree of interstitial porosity, while the redox reaction could contribute to good dispersion of cobalt and manganese species. Moreover, the as-prepared Co x Mn1–x O y catalyst worked well in the presence of water vapor (H2O 4.2%, >60 h) or SO2 (100 ppm) and at high temperature (400 °C, > 60 h). The structure MnO2·(CoOOH)2.93 was suggested for the current Co x Mn1–x O y catalyst. This catalyst could be extended to the total oxidation of other typical hydrocarbons (T 90 = 150 °C for ethanol, T 90 = 225 °C for acetone, T 90 = 250 °C for toluene, T 90 = 120 °C for CO, and T 90 = 540 °C for CH4). Scale-up of the synthesis of Co x Mn1–x O y catalyst (1 kg) can be achieved via ball milling, which may provide a potential strategy for real world catalysis.
chemistry, physical,engineering, chemical, applied