Enhanced dielectric breakdown strength and ultra-fast discharge performance of novel SrTiO3 based ceramics system
Abdullah Jan,Hanxing Liu,Hua Hao,Zhonghua Yao,Marwa Emmanuel,Wengao Pan,Atta Ullah,Abdul Manan,Amjad Ullah,Minghe Cao,Arbab Safeer Ahmad
DOI: https://doi.org/10.1016/j.jallcom.2020.154611
IF: 6.2
2020-07-01
Journal of Alloys and Compounds
Abstract:<p>The ceramics (1−x)SrTiO<sub>3</sub>-x (0.93Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.07Ba<sub>0.94</sub>Sm<sub>0.04</sub>Zr<sub>0.02</sub>Ti<sub>0.98</sub>O<sub>3</sub>) abbreviated as ((1−x) ST -x (BNT-BSmZT)) (x = 0, 0.1, 0.2, 0.3) were synthesized via solid-state sintering route. The phase structure, microstructure, electrical properties and energy storage performances of the outlined compositions were investigated using X-ray diffraction, electron microscopy, and dielectric measurement techniques. The X-ray diffraction results reveal structural phase transformation from a perfect cubic structure to a rhombohedral structure as the x value increased from 0 to 0.3. The submicron grain size of ∼0.71 μm was obtained for x = 0.1. The rest of the parameters such as breakdown strength (BDS), energy storage performance, charge-discharge efficiency (η), discharging time, dielectric loss and electrical conductivity were observed to be affected by the homogeneous, compact microstructure and grain size. Herein we report an innovative ST-based lead free ceramics capacitor with the highest breakdown strength (BDS) of 420 kV/cm, an impressive recoverable energy density (W<sub>rec</sub>) of 1.93 J/cm<sup>3</sup>, simultaneously with high efficiency (η) of 80.0%, moreover, low dielectric loss, low electrical conductivity ∼4.7 × 10<sup>−8</sup> S/m at 100 °C and a fast discharge time (∼0.18 μs) in x = 0.1. Our findings in this work suggest that the obtained ceramics system might be a promising candidate for pulsed power technology.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering