Abstract:The presence of excess fluoride ions in drinking water has raised widespread concerns, necessitating the development of effective methods for its removal. Cerium dioxide (CeO 2 ) holds promise as a selective adsorbent for fluoride ions, due to its exceptional affinity for fluoride and stability across a wide pH range. However, the impact of intrinsic properties of CeO 2 on its adsorption characteristics and mechanisms remains unclear. In this study, we prepared a range of CeO 2 materials with diverse intrinsic properties by adjusting the annealing temperature and atmosphere. Through a series of characterization techniques, we discovered a correlation between the content of oxygen vacancies, Ce(III) species, and surface hydroxyl groups (–OH), all of which decreased simultaneously with increasing air annealing temperature. With respect to the adsorption performance, the highest fluoride adsorption capacity of 111.1 mg g −1 was observed in un-CeO 2 , representing the nanomaterials with the highest oxygen vacancies. This capacity gradually decreased to 29.1 mg g −1 in 800-CeO 2 . Following fluoride adsorption, the oxygen vacancy density, Ce(III) content, and surface –OH content of all CeO 2 materials decreased. When CeO 2 materials were annealed in H 2 for 1 h, the F − adsorption density increased due to the formation of more oxygen vacancies and surface –OH. Based on our findings, we conclude that oxygen vacancies play a critical role in determining whether fluoride ions can successfully exchange with surface –OH groups and enter the crystal lattice of CeO 2 , which significantly affects the adsorption performance. The pivotal role of oxygen vacancies, as proposed in this study, provides a valuable direction for future research aimed at enhancing the fluoride adsorption performance of CeO 2 .

Preparation of a Novel CeO2/SiO2 Adsorbent and Its Adsorption Behavior for Fluoride Ion

Preparation of a novel CeO<sub>2</sub>/SiO<sub>2</sub> adsorbent and its adsorption behavior for fluoride ion

Adsorption of Fluoride Ions Onto Non-Thermal Plasma-Modified Ceo2/Al2o3 Composites

Preparation of CeO2@SiO2 Microspheres by a Non-sintering Strategy for Highly Selective and Continuous Adsorption of Fluoride Ions from Wastewater

Preparation of CeO2/SiO2 Adsorbent and Its Adsorption for Iodate

Preparation of Al–Ce Hybrid Adsorbent and Its Application for Defluoridation of Drinking Water

Mn–Ce oxide as a high-capacity adsorbent for fluoride removal from water

Novel MOF(Zr)-on-MOF(Ce) adsorbent for elimination of excess fluoride from aqueous solution

Efficient removal of fluoride by hierarchical Ce–Fe bimetal oxides adsorbent: Thermodynamics, kinetics and mechanism

Synthesis of a Novel Ce(III)-incorporated Cross-Linked Chitosan and Its Effective Removal of Fluoride from Aqueous Solution

Removal of Fluoride from Wastewater Solution Using Ce-AlOOH with Oxalic Acid As Modification

Hydrothermal Synthesis, Physical Characterization and Fluoride Adsorption of TiO2/CeO2

Synthesis and properties of a high-capacity iron oxide adsorbent for fluoride removal from drinking water

The Roles of the Surface Charge and Hydroxyl Group on a Fe−Al−Ce Adsorbent in Fluoride Adsorption

Iron Oxide (Fe3O4)-Supported SiO2 Magnetic Nanocomposites for Efficient Adsorption of Fluoride from Drinking Water: Synthesis, Characterization, and Adsorption Isotherm Analysis

Adsorption of Ce(IV) Ions from Aqueous Solution by Silica Aerogels

Fluoride Removal of a Novel Ultrasonic-Assisted Supported Fe/γ-Al<sub>2</sub>O<sub>3</sub> Adsorbent

Preparation of CaO loaded mesoporous Al2O3: Efficient adsorbent for fluoride removal from water

Removal of fluoride from water using titanium-based adsorbents

Clean Preparation and Characterization of Magnesium Oxide Nanoparticles As Adsorbents for Fluoride Removal from Aqueous Solution

The impact of redox annealing on intrinsic properties and fluoride adsorption performance of CeO 2 nanomaterials