Single-Atom Ru-Implanted Metal–Organic Framework/MnO 2 for the Highly Selective Oxidation of NO x by Plasma Activation
Si Chen,Yi Zhou,Jieyuan Li,Zhaodong Hu,Fan Dong,Yuxiang Hu,Haiqiang Wang,Lianzhou Wang,Kostya Ken Ostrikov,Zhongbiao Wu
DOI: https://doi.org/10.1021/acscatal.0c02001
IF: 12.9
2020-08-12
ACS Catalysis
Abstract:In an attempt to achieve the selective oxidation of NO<sub><i>x</i></sub>, a hybrid catalyst of single-atom-anchored metal organic frameworks (MOF, NH<sub>2</sub>-UiO-66) and MnO<sub>2</sub> was constructed and used in the plasma catalytic process. Isolated Ru sites were successfully implanted into the structure of the MOF by simply stirring the mixed liquor containing both MOF and RuCl<sub>3</sub>, facilitating plasma discharge, NO/NO<sub>2</sub> adsorption, and formation of <sup>•</sup>OH radicals. A special oxo-bridged Zr<sup>4+</sup>–O–Ru<sup>3+</sup> was constructed to accelerate electron transfer and continuous proceeding of the reaction. Directional migration of generated electrons from MOF to Ru sites was witnessed when MOF was activated by plasma-induced "pseudo-photocatalysis". The total (100%) selective plasma-catalytic oxidation of NO<sub><i>x</i></sub> to NO<sub>2</sub><sup>–</sup> and NO<sub>3</sub><sup>–</sup> was achieved at an SIE of 75.3 J/L. The byproduct O<sub>3</sub> was effectively degraded and utilized by MnO<sub>2</sub>, facilitating the deep oxidation of NO<sub><i>x</i></sub>. The facile realization of single atoms would be an ideal way to produce MOF-based catalysts with desired performance. Efficiently combining plasma with single atom-decorated MOF catalysts can provide additional prospects for the plasma-catalytic system.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c02001?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c02001</a>.ICP–MS results, EXAFS fitting, comparison with literatures, FTIR-absorption peaks, experimental diagram, discharge characteristics, SEM and TEM images, XPS, WT and fitting results of the EXAFS spectra, band structure, mean electron energy, IC, long-duration tests, dynamic concentration, catalysts placing downstream, pore size distribution, discharge current, microdischarge, NO/NO<sub>2</sub> adsorption, ESR, FTIR, and addition of water (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c02001/suppl_file/cs0c02001_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, physical