Synthesis and Characterization of Soluble Polyimides Containing Tert-Butyl, Ether Linkages and Bisphenol A Units
Cong-yan Li,Lang Yi,Shu-ting Xu,Wei Huang,De-yue Yan
DOI: https://doi.org/10.11777/j.issn1000.3304.2016.15346
2016-01-01
Acta Polymerica Sinica
Abstract:A novel diamine monomer containing tert. butyl, ether linkages and bisphenol A unit, 2,2-bis(3'- (tert. butyl). 4'-aniline-bisphenyl-4-ehter) propane (4), was designed and synthesized from 2-tert-butylaniline and bisphenol A. Then it was polymerized with several commercial aromatic dianhydrides, including OPDA, PMDA, 6FDA and BPDA, via one. pot method to afford a series of aromatic polyimides. Their chemical structures are confirmed by NMR, FTIR and EA measurements. The number. averaged molecular weights of the resulting PIs are in the range from 1.9 x10(4) to 3.9 x10(4) with PDI from 2.63 to 4.63 by GPC measurements. They exhibit excellent solubility in many organic solvents, such as NMP, DMF, m-cresol, DMAc, THF and CHCl3 etc, which can be attributed to the incorporation of tert. butyl groups and bisphenol A units into their rigid backbones. They can form transparent films by solution casting and the light transparency was equal to or higher than 90% in the visible light range from 400 to 760 nm. The XRD results demonstrate that they are amorphous glassy polymers. Furthermore, their inherent outstanding performance is still retained, including the high 5% weight loss temperature in nitrogen and T-g, good mechanical properties and low water absorption rates.