Abstract:In magnetic tunnel junctions based on iron oxide nanoparticles the disorder and the oxidation state of the surface spin as well as the nanoparticles functionalization play a crucial role in the magnetotransport properties. In this work, we report a systematic study of the effects of vacuum annealing on the structural, magnetic and transport properties of self-assembled ~10 nm Fe3O4 nanoparticles. The high temperature treatment (from 573 to 873 K) decomposes the organic coating into amorphous carbon, reducing the electrical resistivity of the assemblies by 4 orders of magnitude. At the same time, the 3Fe2+/(Fe3++Fe2+) ratio is reduced from 1.11 to 0.13 when the annealing temperature of the sample increases from 573 to 873 K, indicating an important surface oxidation. Although the 2 nm physical gap remains unchanged with the thermal treatment, a monotonous decrease of tunnel barrier width was obtained from the electron transport measurements when the annealing temperature increases, indicating an increment in the number of defects and hot-spots in the gap between the nanoparticles. This is reflected in the reduction of the spin dependent tunneling, which reduces the interparticle magnetoresistance. This work shows new insights about influence of the nanoparticle interfacial composition, as well their the spatial arrangement, on the tunnel transport of self-assemblies, and evidence the importance of optimizing the nanostructure fabrication for increasing the tunneling current without degrading the spin polarized current.

Controlling the assembly and spin transport of tetrathiafulvalene carboxylate coated iron oxide nanoparticles

Tuning Electron-Conduction and Spin Transport in Magnetic Iron Oxide Nanoparticle Assemblies via Tetrathiafulvalene-Fused Ligands.

Enhancing Magnetoresistance in Tetrathiafulvalene Carboxylate Modified Iron Oxide Nanoparticle Assemblies.

Interfacial Composition and Microstructure of Fe3o4 Magnetic Tunnel Junctions

Enhancing low-field magnetoresistance in magnetite nanoparticles via zinc substitution.

Controlled assembly of Fe3O4 magnetic nanoparticles on graphene oxide.

Electrostatic self-assembly of Fe3O4 nanoparticles on carbon nanotubes

Controlled Evaporative Self-Assembly of Fe3O4 Nanoparticles Assisted by an External Magnetic Field

Fabrication of "Tadpole"-Like Magnetite/Multiwalled Carbon Nanotube Heterojunctions and Their Self-Assembly under External Magnetic Field

Controllable Synthesis Of Hollow Alpha-Fe2o3 Nanostructures, Their Growth Mechanism, And The Morphology-Reserved Conversion To Magnetic Fe3o4/C Nanocomposites

Controlled Phase and Tunable Magnetism in Ordered Iron Oxide Nanotube Arrays Prepared by Atomic Layer Deposition.

Preparation and Magnetic Properties of L10–FePt/TiO2 Nanocomposite Thin Films

A facile solution phase synthesis of directly ordering monodisperse FePt nanoparticles

Assembly, Alignment and Tunable Optical Properties of Montmorillonite with Superparamagnetic Coating

Chemical Synthesis, Structure and Magnetic Properties of Co Nanorods Decorated with Fe3O4 Nanoparticles

Tuning Structure and Properties of a Ferromagnetic Organic Semiconductor via a Magnetic Field-Modified Reduction Process

Monolayer-directed assembly and magnetic properties of FePt nanoparticles on patterned aluminum oxide

Large Magnetoresistance in Fe3o4/Molecule Nanoparticles

Tuning Crystal Structure and Magnetic Property of Dispersible FePt Intermetallic Nanoparticles

Superparamagnetic sub-5 nm Fe@C nanoparticles: isolation, structure, magnetic properties, and directed assembly.

Annealing effects on the magnetic and magnetotransport properties of iron oxide nanoparticles self-assemblies