Nano/micro-structures and Mechanical Properties of Ultra-High Performance Concrete Incorporating Graphene with Different Lateral Sizes
Sufen Dong,Yanlei Wang,Ashraf Ashour,Baoguo Han,Jinping Ou
DOI: https://doi.org/10.1016/j.compositesa.2020.106011
IF: 9.463
2020-01-01
Composites Part A Applied Science and Manufacturing
Abstract:The performance of cement-based materials can be controlled and tailored by adjusting the characteristics of reinforced nano inclusions. Therefore, the lateral size effect of graphene on the nano/micro-structures of ultra-high performance concrete (UHPC) was explored, and then the mechanical properties were investigated to analyze the structure-property correlation of composites in this paper. The test results show that due to nucleation site effect and the formation of core-shell elements, incorporating graphene with lateral size of > 50 mu m improves the polymerization degree and mean molecule chain length of C-S-H gel by 242.6% and 56.3%, respectively. Meanwhile, the porosity and average pore volume of composites is reduced by 41.4% and 43.4%. Furthermore, graphene can effectively inhibit the initiation and propagation of cracks by crack-bridging, crack-deflection, pinning and being pulled-out effect, and the wrinkling characteristic is conducive to the enhancement of pinning effect. These improvements on nano- and micro- structures result in that the compressive strength, compressive toughness and three-point bending modulus of UHPC are increased by 43.5%, 95.7% and 39.1%, respectively, when graphene with lateral size of > 50 mu m and dosage of 0.5% is added. Compared to graphene with lateral size of > 50 mu m graphene with average lateral size of 10 mu m has less folds and larger effective size, then reducing the distance between core-shell elements. Hence, the addition of graphene with average lateral size of 10 mu m leads to 21.1% reduction for Ca(OH)(2) crystal orientation index, as well as 30.0% increase for three-point bending strength. It can be, therefore, concluded that the lateral size of graphene obviously influences the nano/micro-structures of UHPC, thus leading to the significantly different reinforcing effects of graphene on mechanical behaviors of UHPC.