Microstructure and Mechanical Properties of Ti2AlNb Alloy and C/C Composite Joints Brazed with Ag–Cu–Zn and Ag–Cu–Zn/Cu/Ag–Cu–Ti Filler Metals
Hao Zhitao,Wang Dongpo,Yang Zhenwen,Wang Ying
DOI: https://doi.org/10.1016/j.acme.2019.04.008
IF: 4.042
2019-01-01
Archives of Civil and Mechanical Engineering
Abstract:C/C composite was successfully joined to Ti 2 AlNb alloy with inactive filler metal, Ag—Cu—Zn filler. In addition, a designed composite interlayer, Ag—Cu—Zn/Cu/Ag—Cu—Ti, was used to improve the properties of brazed joints. AlCu 2 Ti compound blocks were formed in brazing seam and the double reaction layers adjacent to C/C composite were AlCu 2 Ti and TiC when Ag—Cu—Zn filler was used to join C/C composite and Ti 2 AlNb. With the increase of brazing temperature and time, the amount of AlCu 2 Ti compound blocks increased and tended to accumulate together nearby the C/C composite, the double reaction layers thickened as well. In order to avoid the serious accumulation of brittle AlCu 2 Ti compound nearby C/C composite, Cu foil was added between the Ag—Cu—Zn filler and Ti 2 AlNb. Soft Cu but not brittle AlCu 2 Ti existed nearby the C/C composite with the addition of Cu foil, which is beneficial for the relief of residual stress near the C/C composite, and the shear strength of joint improved obviously. With the barrier of Cu foil, the thickness of reaction layers adjacent to C/C composite could be controlled easily by the addition of Ag—Cu—Ti foil. Correspondingly, the shear strength of this joint reached at 28 MPa, which was close to that of C/C itself.