IN SITU MONITORING OF OSTEOSARCOMA CELLS ON SURFACE-MODULATED SILICON NITRIDE AND TITANIUM BIOMATERIALS

Bryan J. McEntire,Giuseppe Pezzotti,Ryan M. Bock,Wenliang Zhu,Elia Marin,Tetsuya Adachi,B.S. Bal

2017-01-01

Journal of Bone and Joint Surgery - British Volume

Abstract:Introduction Due to its remarkable stoichiometric flexibility and surface chemistry, hydroxyapatite (HAp) is the fundamental structural material in all vertebrates. Natural HAp9s properties inspired an investigation into silicon nitride (Si 3 N 4 ) to see if similar functionality could be engineered into this bioceramic. Biological and in situ spectroscopic analyses were used to monitor the response of osteosarcoma cells (SaOS-2) to surface-modulated Si 3 N 4 and a titanium alloy after long-term in vitro exposure. Materials and Methods Four groups of Si 3 N 4 discs, O12.7×1.0mm, (Amedica Corporation, Salt Lake City, UT USA) were subjected to surface treatments: (i) “As-fired;” (ii) HF-etched (5% HF solution for 45 s); (iii) Oxidized (1070°C for 7 h); and (iv) Nitrogen-annealed (1400°C for 30 min, 1.1 bar N 2 gas). 1 Titanium alloy discs (Ti6Al4V, ASTM F136) were used as a control group. SaOS-2 cells cultured for 24 h at 37 ° C were deposited (5×10 5 cells/ml) and incubated on the UV sterilized discs in an osteogenic medium for 7 days at 37°C. Cell proliferation was monitored using scanning electron and laser microscopy. The Receptor Activator of NF-kB Ligand (sRANKL) and the insulin growth factor 1 (IGF-1) were used to evaluate osteoclast formation and cell proliferation efficiency, respectively. In situ Raman spectroscopy was employed to monitor metabolic cell activity. Statistics (n≥3) were analyzed using the Student9s t-test or one-way Analysis of Variance with p Results Results are presented in Figure 1(a)∼(c) for HAp formation, free sRANKL, and IGF-1, respectively. These data indicate that the N 2 -annealed Si 3 N 4 samples had the highest amount of HAp formation followed by the as-fired, oxidized, and HF samples. The Ti-alloy showed moderate HAp formation; but it had a higher amount of free sRANKL as compared to all Si 3 N 4 samples. These data suggest that the Si 3 N 4 represented a friendlier environment for SaOS-2 cell differentiation. The IGF-1 concentration did not differ among the Si 3 N 4 samples, but they were all higher than the Ti-alloy. Higher IGF-1 stimulates cells to proliferate and differentiate. 2 In Figure 2, in situ collected Raman spectra confirmed enhanced formation of HAp on the Si 3 N 4 samples, especially the N 2 -annealed material. Discussion Enhanced apatite formation was found to originate from a high density of positively charged surface groups, including nitrogen vacancies (V N 3+ ) and nitrogen N-N bonds (N 4+ ). 3 These surface charges promoted binding of proteins onto the negatively charged Si 3 N 4 surface. A dipole-like-charge of V N 3+ /N 4+ and SiO − defective sites is proposed as a mechanism to explain the attraction between proteins and the COO − and NH 2+ terminus, respectively. This is analogous to the mechanism occurring in hydroxyapatite where protein groups are displaced by positively charged calcium loci (Ca + ) and off-stoichiometry phosphorus sites (PO 4 2− ). Conclusion Osteoblast proliferation and apatite-growth are important properties in regenerative bone therapies. In general, these properties were pronounced on all of the Si 3 N 4 substrates; but achieved maximum values on the N 2 -annealed Si 3 N 4 .