Abstract:Binary transition metal sulfides are considered to be a promising material for supercapacitors, possessing richer electrochemically active sites and superior electrochemical performance. Metal-organic frameworks (MOFs) are often used as self-sacrificing templates in the preparation of metal sulfides. Usually, direct sulfidation of MOFs tends to cause collapse of the morphological structure and blockage of the ion transport channels, so that the morphology of the original MOF template can be well preserved by using pyrolysis followed by S2- ion exchange. In this paper, we first prepared NiCo-MOF-74 on nickel foam by an in situ transformation method from layered double hydroxides (LDHs) through a ligand exchange reaction. Then, CoNi2S4 was synthesized in two steps involving the pyrolysis of NiCo-MOF-74 and a subsequent S2- ion exchange reaction. Compared with direct sulfidation, this synthetic strategy can well maintain the rod-like morphology of MOF-74 arrays and prevent structural collapse. The surface of CoNi2S4 has a fine nanosheet structure, which exposes more active sites and shows a high specific capacitance of 7.50 F cm-2 at 2 mA cm-2 and an excellent Coulomb efficiency (96.32%). In addition, the hybrid supercapacitor assembled with activated carbon shows a high energy density of 0.64 mW h cm-2 at a power density of 1.64 mW cm-2 and a high capacitance retention of 88.39% after 5000 cycles. These results indicate that rod-shaped CoNi2S4 can be controllably prepared from MOF-74 involving an exchange reaction and has promising application in high-performance supercapacitors.

Performance Comparison of NiCo 2 O 4 and NiCo 2 S 4 Formed on Ni Foam for Supercapacitor

NiCo2S4@Ni3S2 Hybrid Nanoarray on Ni Foam for High-Performance Supercapacitors

Controlled Preparation of CoNi2S4 Nanorods Derived from MOF-74 Nanoarrays Involving an Exchange Reaction for High Energy Density Supercapacitors.

Formation of Bimetallic Metal-Organic Framework Nanosheets and Their Derived Porous Nickel-Cobalt Sulfides for Supercapacitors.

Characterization of NiCo2 O4 as high-performance supercapacitor electrode materials

High-Performance Ni-Co Sulfide Nanosheet-Nanotubes Grown on Ni Foam As a Binder Free Electrode for Supercapacitors

A Few Atoms Thick Nickel–Cobalt Oxides Mesoporous Nanosheets and Their Arrays on Ni Foam for Supercapacitors with Ultra-Long Cycling Lifespan

Comparing Different Microstructures of CoS Formed on Bare Ni Foam and Ni Foam Coated Graphene and Their Supercapacitors Performance

In Situ Growth of Nico2s4 Nanotube Arrays on Ni Foam for Supercapacitors: Maximizing Utilization Efficiency at High Mass Loading to Achieve Ultrahigh Areal Pseudocapacitance

Nanostructured nickel-cobalt sulfide grown on nickel foam directly as supercapacitor electrodes with high specific capacitance

In situ growth of NiCo2O4 nanosheets arrays on Ni foam for high-performance supercapacitor

In‐Situ Colloidal Synthetic Route to Monodispersed NiCo2S4 Nanoparticles over Nickel Foam for High‐Performance Supercapacitive Charge Storage

Synthesis of NiCo2S4-based nanostructured electrodes supported on nickel foams with superior electrochemical performance

Surfactant Dependence of Nanostructured NiCo2S4 Films on Ni Foam for Superior Electrochemical Performance

Heterostructured Nanocomposites of NiCo–S@Ni(OH)2 on Ni Foam for High-Performance Supercapacitors

Double‐Layer MnCo2S4@Ni‐Co‐S Core/Shell Nanostructure on Nickel Foam for High‐Performance Supercapacitor

Ni Counterpart-Assisted Synthesis of Nanoarchitectured Co3O4/CoS/Ni(OH)2@Co Electrode for Superior Supercapacitor

Spinel FeCo2S4 Nanoflower Arrays Grown on Ni Foam As Novel Binder-Free Electrodes for Long-Cycle-life Supercapacitors

Supercapacitor performance of porous nickel cobaltite nanosheets

MOF-Derived Ultrathin NiCo-S Nanosheet Hybrid Array Electrodes Prepared on Nickel Foam for High-Performance Supercapacitors

Controllable Preparation of Nanoporous Ni 3 S 2 Films by Sulfuration of Nickel Foam As Promising Asymmetric Supercapacitor Electrodes