Abstract:Hybrid organic-inorganic (HOI) based on f-PMMA-SiO2 materials were synthesized by in situ polymerization of methyl methacrylate (MMA) monomer and tetraethoxysilane (TEOS) precursor with the assistance of 3-trimethoxysilyi-propyl-methacrylate (KH-570) as coupling agent. Dye-ionic liquids and the ionic liquid 1-butyl-3-methylimidazolium bis(trifluoromethane sulfonyl)imide [Bmim][NTf2] and 1-butyl-3-methylimidazolium methyl orange [Bmiml[MO] were used as guests for the synthesis of pH-responsive functional poly(methylmethacrylate) (f-PMMA-SiO2) ionogels. The pendent groups of KH-570 allow its linkage to both the silica and MMA, leading to a uniform composite. Optical inspection of the ionogels suggests that the materials are transparent and homogeneous without macroscopic defects. The hybrid ionogels possess a high ionic conductivity of 10(-4) S cm(-1) at 373 K. The bulky gel shows tunable mechanical stability with compressive strength up to 4 MPa that is markedly dependent on the f-PMMA and the ionic liquids incorporation. In particular, color change is clearly observed when the ionogels exposed to proton-containing solution. Moreover, HOI ionogels exhibit significantly enhanced structural integrity in both proton-containing aqueous and organic solution. The resulting material is thus an interesting prototype of flexible, stable and transparent ionogels combining the mechanical properties of the hybrid with the functionality of the ionic liquids. (C) 2017 Elsevier B.V. All rights reserved.

Hybrid Organic-Inorganic Dyeionogels: Reversibly Ph-Responsive Materials Based Dye-Ionic Liquids with Improved Structural Stability and Flexibility