Abstract:Polymeric nitrogen have been recognized to be a new type of high-energy density materials (HEDMs). However, the polymeric nitrogen structures formed under high-pressure and high-temperature conditions are usually in poor thermodynamic stability. Confinement strategy is conductive to the stabilization of the high-pressure phase of polymeric nitrogen structures and provides a new modulation approach for the polymerization of nitrogen. In this paper, nitrogen molecules were confined into the boron nitride nanotubes (N 2 @BNNTs) under high-pressure conditions. The pressure-induced polymerization of nitrogen in N 2 @BNNTs samples with varied nitrogen content and the stabilities of polymeric nitrogen structures were characterized by high-pressure in situ Raman spectroscopy method. In the N 2 @BNNTs sample with higher nitrogen content, the confined N 2 present different Raman spectral response under pressure compared the that of N 2 with confinement, but both of them were transformed into cg-N structure after laser heating at around 123 GPa. With pressure down to 40 GPa, the unconfined cg-N decomposes and release huge energy, which affects the stability and results in the decomposition of the confined cg-N. Under ambient conditions, the confined N 2 is suggested to be stabilized in the liquid phase. In the N 2 @BNNTs sample with lower nitrogen content, the confined N 2 transforms into new polymeric nitrogen structures, which possess N=N double bonds with different bond lengths close to the those in the N 3 - anion and N 4 + clusters, respectively, after laser-heating in the pressure range of 122-150 GPa. This polynitrogen structure is stable with pressure down to 25 GPa. This work provides new insights and route for the synthetization and stabilization of polymeric nitrogen structures.

A Novel Polymerization of Nitrogen in Beryllium Tetranitride at High Pressure

High-pressure Synthesis of Ultraincompressible Hard Rhenium Nitride Pernitride Re-2(N-2)(N)(2) Stable at Ambient Conditions

Exotic stable cesium polynitrides at high pressure

High-pressure and high-temperature induced polymerization of confined nitrogen

Novel Rubidium Poly-Nitrogen Materials at High Pressure

Layered Polymeric Nitrogen in RbN3 at High Pressures

Pressure-Driven Ne-Bearing Polynitrides with Ultrahigh Energy Density

High-energy-density and superhard nitrogen-rich B-N compounds

Pressure-stabilized polymerization of nitrogen in alkaline-earth-metal strontium nitrides

Pressure-Induced High-Energy-Density BeN 6 Materials: First-Principles study

Novel Potassium Polynitrides at High Pressures

Boron Phosphorus Nitride at Extremes: PN6 Octahedra in the High-Pressure Polymorph β-BP3 N6

Novel high-pressure phases of nitrogen-rich Y-N compounds

Highly Condensed and Super‐Incompressible Be2PN3

High-pressure Synthesis of Cobalt Polynitrides: Unveiling Intriguing Crystal Structures and Nitridation Behavior

Pressure-Induced Boron Nitride Nanotube Derivatives: 3d Metastable Allotropes

Stability of new structures of phosphorous-nitrogen solids at high pressure

Nitrogen-rich GaN5 and GaN6 As High Energy Density Materials with Modest Synthesis Condition

Polymerization of Nitrogen in Cesium Azide under Modest Pressure

Formation of the -N(no)n(no)- Polymer at High Pressure and Stabilization at Ambient Conditions

Cobalt–Nitrogen Compounds at High Pressure