Phase Transformation and Dielectric Properties of Bi2((Zn1/3Nb2/3)1-xTix)2O7 Ceramics

Siyuan Dong,Xiaojian Fan,Xiaoli Wang,Ruyan Guo,Amar S. Bhalla

DOI: https://doi.org/10.1080/00150193.2017.1282792

2017-01-01

Ferroelectrics

Abstract:Bi-2((Zn1/3Nb2/3)(1-x)Ti-x)(2)O-7 weberite ceramics with 0.3 <= x <= 0.45 were synthesized using solid-state reaction method. Except Bi-2((Zn1/3Nb2/3)(0.7)Ti-0.3)(2)O-7 with single body-centered orthorhombic weberite phase, the orthorhombic weberite phase of the other compositions changes with sintering temperatures. End-centered orthorhombic weberite is the phase of the ceramics sintered at lower temperatures. With increasing sintering temperature, the end-centered orthorhombic weberite phase transforms into body-centered orthorhombic weberite phase gradually. Although the crystal structures are sensitive to the chemistries and synthesizing conditions, the dense ceramics of Bi-2((Zn1/3Nb2/3)(1-x)Ti-x)(2)O-7 show similar dielectric permittivity epsilon of similar to 160. Their temperature coefficients of capacitance TCC vary from -150 to -280 ppm/degrees C with increasing Ti content. High epsilon, low tan delta (<0.003) and low sintering temperature (similar to 950 degrees C) make the Bi-2((Zn1/3Nb2/3)(1-x)Ti-x)(2)O-7 ceramics are competitive candidates for multiplayer ceramics capacitors and low-temperature co-fired ceramics materials.