Abstract:Introduction of mesopore is critical for applications where mass-transport limitations within microporous networks, especially for zeolite with one-dimensional microporous network, hinder their performance. Generally, the creation of mesopore in zeolite through a direct synthesis route is strongly dependent on complex and expensive organic molecules, which limits their commercial application. Here, we successfully developed a facile synthesis route for preparing ZSM-48 zeolite (*MRE topology) with ultralarge mesoporosity in which typical 1,6-hexylenediamine worked as an organic structure-directing agent, innovatively assisted by a simple crystal growth modifier (tetraethylammonium bromide, TEABr). The working mechanism of TEABr during crystallization was revealed and proposed on the basis of TEM, thermal gravimetric mass spectrum, and 13C cross-polarization magic angle spinning NMR characterization results. In the process, TEA+ ions preferentially interacted with the solid during the induction period, which effectively suppressed the aggregation of ZSM-48 primary nanorods. As a result, ultralarge mesoporosity of 0.97 cm3·g–1 was constructed through the stacking of the nanorods. Interestingly, TEA+ ions only took part in the crystallization process and did not occlude in the pores of the final zeolites indicating its potential in recyclability. Moreover, similar synthesis strategy could be applied for the preparation of hierarchical ferrierite zeolites, implying the universality of this strategy. Compared with a conventional sample, ZSM-48 zeolite with ultralarge mesoporosity showed superior catalytic stability in the m-xylene isomerization reaction due to its significantly enhanced diffusion and mass transfer capability, which will greatly promote the practical application of ZSM-48 zeolite.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c09137?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c09137</a>.Ferrierite zeolite synthesis; SEM images; 13C CP/MAS NMR spectra; MX conversion and PX selectivity; NH3-TPD profiles; adsorption isotherms of MX; TG results; and textural properties of samples before and after reaction (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c09137/suppl_file/am1c09137_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Engineering a Tubular Mesoporous Silica Nanocontainer with Well-Preserved Clay Shell from Natural Halloysite

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

High-Surface-Area Zeolitic Silica with Mesoporosity

A novel mesoporous silica-clay composite and its thermal and hydrothermal stabilities

Mesoporous silicas of hierarchical structure by hydrothermal surfactant-templating under mild alkali conditions

Direct synthesis of hydrothermally stable micro–mesoporous silicas templated by unsaturated α-linolenic acid self-assemblies under high temperature hydrothermal conditions

Synthesis of Nanosized Multilayered Silica Vesicles with High Hydrothermal Stability

Fabrication of Core-Shell Structured Mesoporous Silica Nanospheres with Dually Oriented Mesochannels Through Pore Engineering

Controllable Architecture of Mesoporous Double-Nanoshell SiO2/TiO2 Hollow Tube Based on Layer by Layer Method

Mechanistic Insight into the Synthesis and Morphological Evolution of Superhydrophobic Silica Nanotubes

Rapid and Controlled In Situ Growth of Noble Metal Nanostructures within Halloysite Clay Nanotubes

Genetic structure of Mediterranean populations of the sandfly Phlebotomus papatasi by mitochondrial cytochrome b haplotype analysis

Mesoporous silica obtained with methyltriethoxysilane as co-precursor in alkaline medium

One-Pot Synthesis of Catalytically Stable and Active Nanoreactors : Encapsulation of Size-Controlled Nanoparticles within a Hierarchically Macroporous Core

Facile Synthesis of Hierarchical Nanosized Single‐Crystal Aluminophosphate Molecular Sieves from Highly Homogeneous and Concentrated Precursors

Direct Preparation of *MRE Zeolites with Ultralarge Mesoporosity: Strategy and Working Mechanism

The Size-Controllable Synthesis of Nanometer-Sized Mesoporous Silica in Extremely Dilute Surfactant Solution

Synthesis and Characterization of Ordered Mesoporous Aluminosilicate Molecular Sieve from Natural Halloysite

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

The Synthesis of Porous Materials with Macroscopically Oriented Mesopores Interconnected by Branched Mesopores

In situ Fabrication of Multi-Walled Carbon Nanotubes/Silica Hybrid Colloidosomes by Pickering Emulsion Templating Using Trialkoxysilanes of Opposite Polarity