Thermally-induced phase transformations in Na0.5Bi0.5TiO3-KNbO3 ceramics

Ge Wang,Yizhe Li,Claire A. Murray,Chiu C. Tang,David A. Hall

DOI: https://doi.org/10.1111/jace.14856

IF: 4.186

2017-01-01

Journal of the American Ceramic Society

Abstract:The structures and functional properties of Na0.5Bi0.5TiO3-xKNbO(3) (NBT-xKN) solid solutions, with x in the range from 0.01 to 0.09, were investigated using a combination of high-resolution synchrotron X-ray powder diffraction (SXPD) and ferroelectric property measurements. For low KN contents, an irreversible transformation from cubic to rhombohedral phases was observed after the application of a high electric field, indicating that the polar nanoregions (PNRs) in the unpoled state can be transformed into metastable long-range ordered ferroelectric domains in the poled state. In contrast, the near-cubic phase of the unpoled ceramics was found to be remarkably stable and was retained on cooling to a temperature of -175 degrees C. Upon heating, the field-induced metastable ferroelectric rhombohedral phase transformed back to the nanopolar cubic state at the structural transformation temperature, T-ST, which was determined as approximately 225 degrees C and 125 degrees C for KN contents of 3% and 5% respectively. For the field-induced rhombohedral phase in the poled specimens, the pseudo-cubic lattice parameter, a(p), exhibited an anomalous reduction while the inter-axial angle increased towards a value of 90 degrees on heating, resulting in an overall increase in volume. The observed structural changes were correlated with the results of temperature-dependent dielectric, ferroelectric and depolarization measurements, enabling the construction of a phase diagram to define the stable regions of the different ferroelectric phases as a function of composition and temperature.