Abstract:Biomass-derived porous carbons have received an extensive importance as effective electrode materials owing to their abundance and low cost. The unique porous architectures and large specific surface areas of biomass are beneficial for manipulating the charge storage performance of assembled supercapacitor devices. Here, we demonstrate nitrogen and phosphorus self-doped hierarchical porous carbon (N/P-HPC) derived from yeast (Y) and phytic acid (PA) precursors via freeze-drying-assisted esterification reaction and pyrolysis treatment. The supercapacitive performance and charge storage capability of N/P-HPC were regulated by optimizing the Y/PA composition and controlling the carbonization temperature. Accordingly, the resultant N/P-HPC-Y:PA(2:1)-800 (fabricated with an optimized Y:PA ratio of 2:1 and carbonized at 800 °C) reveals a high specific surface area of 978 m2 g−1 and a large pore volume of 0.592 cm3 g−1. As an electrode material, N/P-HPC-Y:PA(2:1)-800 delivers a high specific capacitance of 432 F g−1 at a current density of 1 A g−1 and can sufficiently retain about 250 F g−1 at 20 A g−1 under a three-electrode cell configuration in 1.0 M H2SO4 electrolyte. Moreover, the as assembled symmetric supercapacitor device operated with the N/P-HPC-Y:PA(2:1)-800 as both positive and negative electrode material exhibits an energy density of 13.6 Wh kg−1 at a power density of 500 W kg−1. Even at a larger current density of 20 A g−1, the device maintains an energy density of 10.4 Wh kg−1 and a maximum power density of 10 kW kg−1. The constructed device displays a large capacitance retention of 93.3% after 10 000 charge/discharge times at a higher current density of 10 A g−1, manifesting the enhanced cycling stability.

Lignocellulose-derived Porous Phosphorus-Doped Carbon As Advanced Electrode for Supercapacitors

A Novel Synthesis of Hierarchical Porous Carbons from Interpenetrating Polymer Networks for High Performance Supercapacitor Electrodes

Nitrogen and Phosphorus Co-doped Porous Carbon for High-Performance Supercapacitors

Facile synthesis of N/P co-doped carbons with tailored hierarchically porous structures for supercapacitor applications

Fabricating N, P-Codoped Hierarchical Porous Carbons from Lignin via Assembled Templating and Activation Strategy for High-Performance Supercapacitors

Phosphorus-doped thick carbon electrode for high-energy density and long-life supercapacitors

Phosphorus-doped 3D hierarchical porous carbon for high-performance supercapacitors: A balanced strategy for pore structure and chemical composition

Strategic N/P self-doped biomass-derived hierarchical porous carbon for regulating the supercapacitive performances

Chitosan-Based Synthesis of O, N, and P Codoped Hierarchical Porous Carbon as Electrode Materials for Supercapacitors

Sustainable Synthesis of Phosphorus- and Nitrogen-Co-doped Porous Carbons with Tunable Surface Properties for Supercapacitors

Facile Synthesis of Nitrogen-Doped Porous Carbon As Robust Electrode for Supercapacitors

Phosphorus/sulfur Co-doped Porous Carbon with Enhanced Specific Capacitance for Supercapacitor and Improved Catalytic Activity for Oxygen Reduction Reaction

Oxygen/phosphorus co-doped porous carbon from cicada slough as high-performance electrode material for supercapacitors

A micropore-dominant N,P,S-codoped porous carbon originating from hydrogel for high-performance supercapacitors mediated by phytic acid

Porous Carbon Electrode from Starch Soluble for Realizing High‐Performance Supercapacitor

P-doped porous carbon composite by caustic pyrolysis of copolymer as supercapacitor

Synthesis and electrochemical study of phosphorus-doped porous carbon for supercapacitor applications

Heteroatoms Doped Porous Carbon Derived from Waste Potato Peel for Supercapacitors

Nitrogen, Phosphorus Co-doped Carbon Obtained from Amino Acid Based Resin Xerogel as Efficient Electrode for Supercapacitor

Thiocyanogen-modulated N, S Co-doped lignin hierarchical porous carbons for high-performance aqueous supercapacitors

Multicomponent doped hierarchically porous carbon derived from natural polyelectrolyte for high‐performance supercapacitors