Biomimetic Synthesis of Calcium Carbonate Films on Bioinspired Polydopamine Matrices

Zhenni Li,Bo Peng,Ziwei Deng

DOI: https://doi.org/10.1007/s11998-016-9898-x

2017-01-01

Journal of Coatings Technology and Research

Abstract:We combine the active surface of polydopamine (PDA) with the biomimetic mineralization of CaCO 3 to obtain the macroscopically continuous CaCO 3 films under mild conditions. In this approach, the organic matrices were adhesive PDA coatings, which were dip-coated on silicon wafers by the self-polymerization of dopamine in an alkaline aqueous solution (pH 8.5). The inorganic layers were CaCO 3 films, which were formed in a CaCl 2 solution in the presence of poly(acrylic acid) (PAA) via a CO 2 diffusion method. During the biomimetic mineralization, amorphous calcium carbonate (ACC) was formed on PDA matrices with the help of PAA, which, subsequently, was transformed into a flat continuous calcite film on the PDA matrices. As the mineralization time increased, a new layer of CaCO 3 crystals was formed over the calcite and, as a result, led to continuous CaCO 3 films with rough surfaces. The thicknesses of CaCO 3 films can be controlled by tuning the mineralization time. Our approach may provide a simple, yet efficient way for the preparation of macroscopically continuous organic–inorganic composite CaCO 3 films under mild conditions. Moreover, superhydrophobic surfaces can be successfully achieved via a hydrophobic modification of the rough CaCO 3 films, which make them suitable candidates for a variety of superhydrophobic applications, such as self-cleaning surfaces or anticorrosion, antiadhesive coatings.