Preparation of Polyoxometalate-Chalcone Hybrid and Its Photo-Polymerization Property

ZHANG Jie,LONG Yong,XUAN WeiMin,LIN ChangGen,SONG YuFei
DOI: https://doi.org/10.1360/n972016-01262
2017-01-01
Abstract:Photo-sensitive polyoxometalate-based hybrid materials have attracted much attention in recent years due to their unique photo-responsive properties. Here we represent a new type of photo-sensitive polyoxometalate-based hybrid by covalently tethering chalcone moieties onto Anderson cluster. Various techniques including nuclear magnetic resonance (NMR), Fourier transform infrared spectoscopy (FT-IR), electrospray ionization-mass spectrometry (ESI-MS) and single-crystal X-ray diffraction have been utilized to characterize the structure and composition of the resultant hybrid. The 1 H and 13 C NMR spectra show well resolved peaks that can be unambiguously assigned and are in good accordance with the molecular structure. Characteristic stretching vibrations of MO and Mo–O–Mo bonds can be found at 940 and 668 cm - 1 in the FT-IR spectrum respectively, whilst the chalcone moieties give stretching bands at 1665/1593 cm –1 (C=O–C=C) and 1568/1511 cm - 1 (C=C). The ESI-MS spectrum of the hybrid provides us more convincing structural in- formations. For instance, the isotopic peaks observed at m / z =2167.81 can be clearly ascribed to the anionic fragment of {[( n -C 4 H 9 ) 4 N] 2 [(MnMo 6 O 24 ){(CH 2 ) 3 CNHCOCH 2 OC 6 H 4 C 2 H 2 COC 6 H 5 } 2 ]} - , suggesting the successful modification of Anderson cluster with chalcone molecules. Single-crystal X-ray diffraction analysis reveals that the hybrid crystallizes in a mono-clinic system with a C2 / c space group, where organic chalcone moieties are covalently bonded to the Anderson cluster via μ 3 -oxo bridging ligands. The photo-polymerization properties of the hybrid have been investigated in detail using UV-Vis spectroscopy, 1 H NMR, and gel permeation chromatography. For example, when irradiated at UV light of 365 nm the hybrid undergoes a [2 π +2 π ] cycloaddition reaction, leading to an absorbance decrease at wavelength of 332 nm in the UV-Vis spectrum. Meanwhile, a new absorbance peak attributed to the generated cyclobutane structure is observed at 245 nm. This process gives a total photo-polymerization conversion of 37.45%, and is found able to restore when exposed to UV light of 254 nm. After five cycles of alternative irradiation at 365 and 254 nm, the amount of the hybrid monomer can still maintain at 85% of the original ones. The 1 H NMR spectrum of the hybrid also shows significant changes when irradiated at UV light of 365 nm. Signals of the unsaturated carbonyl groups of the chalcone moieties at δ 7.83 and 7.73 shift to high field after irradiation, and give corresponding cyclobutane signal at δ 4.80. These results are in accordance with the results of UV-Vis spectroscopy. Weight-average molecular weight of the resulting hybrid polymer is 9.78×10 5 g/mol as demonstrated by the gel permeation chromatography analysis. This work may provide a new pathway for the fabrication and functional application of novel photo-sensitive polyoxometalate-based hybrids.
What problem does this paper attempt to address?