Wear and Corrosion Resistant Coatings on Surface of Cast A356 Aluminum Alloy by Plasma Electrolytic Oxidation in Moderately Concentrated Aluminate Electrolytes

Huan-jun Xie,Ying-liang Cheng,Shao-xian Li,Jin-hui Cao,Li Cao

DOI: https://doi.org/10.1016/s1003-6326(17)60038-4

IF: 3.752

2017-01-01

Transactions of Nonferrous Metals Society of China

Abstract:Plasma electrolytic oxidation of a cast A356 aluminum alloy was carried out in aluminate electrolytes to develop wear and corrosion resistant coatings. Different concentrations of 2, 16 and 24 g/L NaAlO2 solutions and a silicate electrolyte (for comparison) were employed for the investigation. Wear performance and corrosion resistance of the coatings were evaluated by WC (tungsten carbide) ball-on-flat dry sliding tests and electrochemical methods, respectively. The results show that the coating formed for a short duration of 480 s in 24 g/L NaAlO2 solution generated the best protection. The coating sustained 30 N load for sliding time of 1800 s, showing very low wear rate of ∼4.5×10−7 mm3/(N·m). A low corrosion current density of ∼8.81×10−9 A/cm2 was also recorded. Despite low α-Al2O3 content of the coating, the compact and nearly single layer nature of the coating guaranteed the excellent performances.