Template-Free Construction of Tin Oxide Porous Hollow Microspheres for Room-Temperature Gas Sensors
Licheng Zhou,Zhixiang Hu,Hua-Yao Li,Jingyao Liu,Yi Zeng,Jingsong Wang,Yifu Huang,Ling Miao,Guangzu Zhang,Yongan Huang,Jianjun Jiang,Shenglin Jiang,Huan Liu
DOI: https://doi.org/10.1021/acsami.1c04651
2021-05-18
Abstract:Porous hollow microsphere (PHM) materials represent ideal building blocks for realizing diverse functional applications such as catalysis, energy storage, drug delivery, and chemical sensing. This has stimulated intense efforts to construct metal oxide PHMs for achieving highly sensitive and low-power-consumption semiconductor gas sensors. Conventional methods for constructing PHMs rely on delicate reprogramming of templates and may suffer from the structural collapse issue during the removal of templates. Here, we propose a template-free method for the construction of tin oxide (SnO<sub>2</sub>) PHMs via the competition between the solvent evaporation rate and the phase separation dynamics of colloidal SnO<sub>2</sub> quantum wires. The SnO<sub>2</sub> PHMs (typically 3 ± 0.5 μm diameter and approximately 200 nm shell thickness) exhibit desirable structural stability with desirable processing compatibility with various substrates. This enables the realization of NO<sub>2</sub> gas sensors having a superior response and recovery process at room temperature. The superior NO<sub>2</sub>-sensing characteristic is attributed to the effective gas adsorption competition on solid surfaces benefiting from efficient diffusion channels, enhancing the interaction of metal oxide solids with gas molecules in terms of the receptor function, transducer function, and utility factor. In addition, the one-step deposition of SnO<sub>2</sub> PHMs directly onto device substrates simplifies the fabrication conditions for semiconductor gas sensors. The desirable structural stability of PHMs combined with the functional diversity of metal oxides may open new opportunities for the design of functional materials and devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c04651?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c04651</a>.Image of the sensor device (Figure S1); SEM images of colloidal SnO<sub>2</sub> quantum wire films prepared by the spin-coating method (Figure S2); SEM images of SnO<sub>2</sub> PHMs based on different substrates (Figure S3); nitrogen adsorption–desorption isotherm (Figure S4); response curve of SnO<sub>2</sub> PHM gas sensors before removing the long-chain ligands (Figure S5); response curves of the SnO<sub>2</sub> PHM sensor at different operating temperatures (Figure S6) and relative humidity values (Figure S7); data expressed as time vs response (Figure S8); response time and recovery time at different operating temperatures (Figure S9); long-term stability of SnO<sub>2</sub> PHM gas sensors (Figure S10); and different molecule-surface adsorption models and adsorption energies of SnO<sub>2</sub> (110 facet) toward O<sub>2</sub> and NO<sub>2</sub> (Figure S11) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c04651/suppl_file/am1c04651_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology