Abstract:The fatigue performance of AlSi10Mg composites decorated with nano-TiB2 particles fabricated through laser powder bed fusion (LPBF) was first experimentally investigated at room temperature and it exhibited superior fatigue resistance compared with other LPBF AlSi10Mg alloys and other reinforced AlSi10Mg composites. Then the fractography was examined and a fracture mechanics-based life prediction method was proposed to correlate the critical defect information (size and location) and fatigue life. To assess the crack growth driving force for critical defects, we employed Murakami's concept of the maximum stress intensity factor (SIF). The modification was made to include the effect of specimen cross-sectional geometry and initiation location since Murakami's method would underestimate the maximum SIF in some cases. Meanwhile, the process of small crack propagation was also considered in modeling, and a unified model to describe crack arrest, small crack growth, and long crack growth was established. By inputting information about defect size and location and external loading conditions, the fatigue life could be evaluated and our results demonstrated good estimation within the [1/4,2] scatter band. Furthermore, an unbroken specimen subjected to the highest external loading was examined using X-ray computed tomography (CT) to characterize the defect population. By incorporating the CT statistical results into our life prediction model, outcomes such as non-propagating cracks or small crack growth without leading to ultimate failure could be obtained, which was consistent with CT findings. Concurrently, CT analysis revealed that the detrimental effect of large inner defects could be less significant than that of small surface defects. Therefore, we propose a novel strategy that combines defect size and location to enhance defect tolerance in additive manufacturing (AM) materials.

Fatigue Crack Growth and Fracture of 30 Wt% B4c/6061al Composites

Study on fracture mechanism and fatigue life prediction for cutting insitu tib2/7050al mmcs

Fatigue Behavior of In-Situ TiB2/7050Al Metal Matrix Composites: Fracture Mechanisms and Fatigue Life Modeling after Milling

Effects of stress state, strain rate, and temperature on fracture behavior of in situ TiB2/2024 Al composite

Fatigue Crack Initiation and Propagation in A356 Alloy Reinforced with in Situ TiB2 Particles

Vibration Fatigue Assessment and Crack Propagation Mechanism of Directionally Solidified Superalloy with Film Cooling Holes

Influence of particulate B4C with high weight fraction on microstructure and mechanical behavior of an Al-based metal matrix composite

Experimental study of the mechanisms of nanoparticle influencing the fatigue crack growth in an in-situ TiB2/Al-Zn-Mg-Cu composite

Deformation Behavior and Damage in B4Cp/6061Al Composites: an Actual 3D Microstructure-Based Modeling

Microstructural correlated damage mechanisms of the high-cycle fatigued in-situ TiB2/Al-Cu-Mg composite

Dynamic Tensile Deformation and Damage of B4C-reinforced Al Composites: Time-resolved Imaging with Synchrotron X-Rays

High Fatigue Performance and Microscopic Mechanisms of In-Situ TiB2/7050Al Composite at Different Temperatures

Crack Initiation and Propagation of Cast A356 Aluminum Alloy under Multi-Axial Cyclic Loadings

Friction and Wear Behaviors of B4c/6061al Composite

High fatigue performance and microscopic mechanisms of in-situ TiB 2 /7050Al composite at different temperatures

Fatigue Behaviors of C/Mo Double-Coated SiC Fiber-Reinforced Ti6Al4V Composites with Varied Interfacial Microstructure

Revealing the complex effects of particle bands on fatigue crack growth in an extruded aluminium matrix composite

Fatigue Performance of Laser Powder Bed Fusion Manufactured TiB2/AlSi10Mg Composite: Experimental Investigation and Fracture Mechanics-Based Life Prediction Model for Defect Tolerance Analysis

Enhancing fatigue crack propagation resistance of heterostructured Al composites and multistage crack mechanisms

Revealing the Effect of Oriented Microstructures on the Anisotropy of Fatigue Crack Propagation Behavior in TiB2/Al-Cu-Mg-Mn Composite

High Cycle Fatigue Behavior of Bulk 6061al Prepared by Cold Spray-Friction Stir Processing Composite Additive Manufacturing