Surface Tuning to Promote the Electrocatalysis for Oxygen Evolution Reaction: From Metal-Free to Cobalt-Based Carbon Electrocatalysts
Yanan Wang,Shuguang Zhang,Xiuxia Meng,Ting Wang,Yu Feng,Weimin Zhang,Yu-Shi He,Yucheng Huang,Naitao Yang,Zi-Feng Ma
DOI: https://doi.org/10.1021/acsami.0c17599
2020-12-29
Abstract:Heterogeneous electrocatalytic reactions only occur at the interface between the electrocatalyst and reactant. Therefore, the active sites are only necessary to be distributed on the surface of the electrocatalyst. Based on this motivation, here, we demonstrate a systematic study on surface tuning for a carbon-based electrocatalyst from metal-free (with the heteroatoms N and S, NS/C) to metal-containing surfaces (with Co, N, and S, CoNS/C). The CoNS/C electrocatalyst was obtained by pyrolyzing the Co precoordinated and <i>p</i>-toluenesulfonate-doped polypyrrole (PPy). It was found that the coordination of Co on the PPy ring tuned the final carbon electrocatalyst into a catalyst with a CoN<sub><i>x</i></sub> moiety-rich surface. In addition, the as-synthesized CoNS/C was determined to have a very high loading of cobalt up to 2.02 wt %. The pyrolysis of the cobalt-containing precursor tends to proceed toward a characteristic of a higher sp<sup>2</sup> carbon content, a higher surface area, and more nitrogen as well as active nitrogen sites than its metal-free counterpart. The most distinguished feature for such a catalyst is that the truly most active component is only distributed on the surface, in contrast with that of the conventional metal–N-based catalyst present throughout the bulky structure. Especially, the electrocatalytic activity toward oxygen evolution reaction (OER) has been investigated experimentally and theoretically. The results showed that the OER performance of the carbon-based electrocatalyst was remarkably boosted after the introduction of Co with an overpotential decrease from 678 to 345 mV at 10 mA cm<sup>–2</sup>. Furthermore, CoNS/C displayed an excellent durability upon a long-term measurement. The apparent activation energy measurements revealed that the metal-rich surface contributed to overcome the energy barrier for OER. In addition, density functional theory calculations have been conducted to explain the correlated OER mechanism. This study is expected to provide an effective strategy for the design and the synthesis of highly active metal–nitrogen-type electrocatalysts with a high metal loading for various electrocatalytic reactions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c17599?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c17599</a>.Raman spectra and XRD patterns of NS/C and CoNS/C; SEM and HR-TEM images of NS/C; XPS survey spectrum of CoNS/C; TGA curves of CoNS/C and etched CoNS/C; calculated mass content of Co according to TGA; survey XPS spectrum and high-resolution C 1s, N 1s, and S 2p of NS/C; N<sub>2</sub> sorption isotherms and BJH desorption pore size distributions of NS/C and CoNS/C; RRDE measurement of the Co–PPy electrode toward OER; LSV curves of CoNS/C electrocatalysts synthesized with various temperatures toward OER; content of N determined using XPS spectra in CoNS/C with different pyrolysis temperatures; fitted parameters for EIS results; LSV curves of CoNS/C and etched CoNS/C toward OER; summary of the overpotentials of the various electrodes at 10 mA cm<sup>–2</sup>; temperature-dependent LSV curves of the corresponding fittings of activation energy of NS/C, CoNS/C, and RuO<sub>2</sub> toward OER; ADT tests of NS/C toward OER; SEM image of CoNS/C and NS/C after the ADT test; survey XPS spectrum and high-resolution N 1s and Co 2p of CoNS/C after the test; DFT calculations; and summary of the OER activity comparison for recent various advanced non-precious-metal-based electrocatalysts (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17599/suppl_file/am0c17599_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology