Permeation Properties of Silica-Zirconia Composite Membranes Supported on Porous Alumina Substrates

So-Jin Ahn,Atsushi Takagaki,Takashi Sugawara,Ryuji Kikuchi,S. Ted Oyama

DOI: https://doi.org/10.1016/j.memsci.2016.12.023

IF: 9.5

2017-01-01

Journal of Membrane Science

Abstract:A hydrogen-selective silica-zirconia composite membrane was prepared on a macroporous alumina support by chemical vapor deposition of tetraethylorthosilicate (TEOS) and zirconium (IV) tert-butoxide (ZTB) at 923K. The resulting membrane had a high H2 permeance of 3.8×10−7molm−2s−1Pa−1 with selectivities over CO2, N2 and CH4 of 1100, 1400 and 3700, respectively. Studies of the temperature dependence of the permeance of He, H2, and Ne demonstrated that the permeation mechanism was similar to that of dense silica membranes, involving solid-state diffusion with jumps of the permeating species between solubility sites. Parameters such as the site density, jump distance, and jump frequency were calculated and were physically plausible, and varied in reasonable manner with the mass and size of He, H2, and Ne. An alternative mechanism involving an activated gas translational mechanism was shown to fit the data but to give physically unrealistic parameters. The silica-zirconia membrane showed hydrothermal stability over a limited testing period of 48h. After exposure to 16mol% water vapor at 923K for 48h, a pure silica membrane showed a 68% decline with a H2 permeance of 4.5×10−8molm−2s−1 Pa−1 and a H2 over N2 selectivity of 800, both of which continued to deteriorate. In comparison, a 10% ZrO2-SiO2 membrane showed a decline of 56% but to a level of 10−7molm−2s−1Pa−1 with a H2 over N2 selectivity of 5700. Importantly, the deterioration largely stabilized at that permeance level.