Abstract:Shape-stabilized phase change materials (SSPCM) offer significant potential in industrial applications, effectively addressing corrosion and thermal stress issues associated with phase change material (PCM) at high temperatures. To advance the large-scale development of SSPCMs, this study innovatively proposes the wet-state extrusion and sintering method to prepare SSPCM particles (SSPCM-P) and characterize them. Solar salt is the PCM, while calcined dolomite is the skeletal support material (SSM). Results indicate successful fabrication of SSPCM-P with salt content below 60 wt% post-sintering, a lower threshold than those achieved via cold-pressing and hot-sintering methods. This is because, during wet mixing and evaporation, salts migrate to the surface of the sample and mixtures with high salt content on the surface tend to bond together during sintering. SEM observations reveal a transparent interface between SSM and PCM pre-sintering, whereas post-sintering, PCM uniformly adheres to the SSM surface, with smaller particle sizes demonstrating enhanced densification. SSPCM-P shows commendable chemical stability, with the enthalpy of melting/solidification for SSPCM-P with 60 % salt content slightly below the theoretical value at 63.6/63.3 J/g. Charging and discharging experiments highlight significantly improved thermal properties of SSPCM-P compared to sensible heat materials, enabling oil heating to higher temperatures. SSPCM-P can maintain stability during recirculation. Furthermore, it is noted that SSPCM-P is unsuitable for vapour applications due to salt precipitation, making direct contact heat transfer with vapour unfeasible. As a solution, the study proposes the application of SSPCM-P in finned tube heat exchangers to circumvent chemical incompatibility issues with heat transfer fluid, leveraging its compact size, ease of preparation, and stacking capabilities. These pivotal findings present new industrial solutions for SSPCM preparation, promising significant technological advancements in energy storage and heat transfer.

Stability and Corrosion Testing of A High Temperature Phase Change Material for Csp Applications

Determination of Thermo-Physical Properties and Stability Testing of High-Temperature Phase-Change Materials for Csp Applications

Preparation and Characterization of Fatty Acid Ternary Eutectic Mixture/Nano-Sio 2 Composite Phase Change Material for Building Applications

A Eutectic Salt High Temperature Phase Change Material: Thermal Stability and Corrosion of SS316 with Respect to Thermal Cycling

Review and characterisation of high-temperature phase change material candidates between 500 C and 700C

Review and Characterisation of High-Temperature Phase Change Material Candidates Between 500 C and 700°C

Characterisation of Promising Phase Change Materials for High Temperature Thermal Energy Storage

Surface evolution of eutectic MgCl2·6H2O-Mg(NO3)2·6H2O phase change materials for thermal energy storage monitored by scanning probe microscopy

Thermal Characteristics of Melting of a Phase Change Material Enhanced by a Stainless-Steel 304 Periodic Structure

Experimental and Numerical Analysis for the Discharge Performance of a High Temperature Phase Change Material with Low-Cost Wire Mesh

Heat transfer characteristics and compatibility of molten salt/ceramic porous composite phase change material

Macro-encapsulation and characterization of chloride based inorganic Phase change materials for high temperature thermal energy storage systems

Preparation and characterization of shape-stable phase change particles: A new option for high-temperature thermal energy storage

Form-stable Na2CO3-NaCl/mullite Phase Change Composite with SiC Enhanced Thermal Conductivity for High Temperature Thermal Storage

Studies of eutectic hydrated salt/polymer hydrogel composite as form-stable phase change material for building thermal energy storage

Preparation and thermal property enhancement of sodium acetate trihydrate-lithium chloride-potassium chloride expanded graphite composite phase change materials

Phase change material mixed with chloride salt graphite foam infiltration for latent heat storage applications at higher temperatures and pressures

A novel super high latent heat ternary eutectic salt for high temperature thermal energy storage

Low-cost magnesium-based eutectic salt hydrate phase change material with enhanced thermal performance for energy storage

Eutectic Na2CO3–NaCl Salt: A New Phase Change Material for High Temperature Thermal Storage

A Shape-Stabilized Mgcl2 Center Dot 6h(2)O-Mg(No3)(2)Center Dot 6h(2)O/Expanded Graphite Composite Phase Change Material With High Thermal Conductivity And Stability