The Role of Melt Memory and Template Effect in Complete Stereocomplex Crystallization and Phase Morphology of Polylactides
Yan-Fei Huang,Zheng-Chi Zhang,Yue Li,Jia-Zhuang Xu,Ling Xu,Zheng Yan,Gan-Ji Zhong,Zhong-Ming Li
DOI: https://doi.org/10.1021/acs.cgd.7b01562
IF: 4.01
2018-01-01
Crystal Growth & Design
Abstract:Stereocomplex crystal (SC) formation induced by thermal treatment is the most promising approach to achieve the heat resistance of polylactides (PLA). However, a hierarchical morphology of SCs, formed under a different thermal environment, is rarely reported although it is crucial for us to understand their enhanced effect on heat resistance. This work examines the morphology of 1:1 stoichiometric blends of poly(L-lactide)/poly(D-lactide) (PLLA/PDLA) after thermal treatment. In order to explore the formation mechanism of the morphology, in situ wide-angle X-ray diffraction (WAXD) was conducted during the entire thermal treatment. Interestingly, a phase separation structure resulting from the melt memory effect of homocrystallites is observed, for the first time, when the amorphous sample was treated at a relatively low temperature (190 degrees C). Upon increase of the treatment temperature to a medium one (210 degrees C), two template effects, that is, the template of unmelted SCs during the isothermal process and new templates formed due to the supercooling during the cooling process, produce different crystallization kinetics, promoting the formation of sunflower-like spherulites. It is worth noting that under this thermal environment, complete SC could be achieved simply, which has never been realized from the melt of a high molecular weight PLLA/PDLA blend. The template effect of unmelted SC also endows the sample thermally treated at high temperature (230 degrees C) with incredibly high crystalline temperature, giving rise to squeezed spherulites. This work sheds light on the mechanism of the SC formation, providing effective guidance for hierarchical morphology control of SC for highly heat deflection resistance and bringing about a facile approach to achieve exclusive SC crystallites in melt processed products.