Rapid Fabrication of Function-Structure-integrated NiTi Alloys: Towards a Combination of Excellent Superelasticity and Favorable Bioactivity

L. Zhang,Z. Y. He,J. Tan,Y. Q. Zhang,M. Stoica,K. G. Prashanth,M. J. Cordill,Y. H. Jiang,R. Zhou,J. Eckert

DOI: https://doi.org/10.1016/j.intermet.2016.11.004

IF: 4.075

2017-01-01

Intermetallics

Abstract:Porous NiTi has brought new expectations to the field of orthopaedic implants due to its excellent mechanical properties such as high strength and superelasticity together with good biocompatibility. In order to facilitate the surrounding bone tissue ingrowth into the implanted porous alloy, reasonably large sized pores and a high amount of porosity are required. There is, however, a major challenge for clinical applications: the higher the porosity, the worse are the mechanical properties and the superelasticity. In this work, therefore, function-structure-integrated NiTi alloys consisting of a central solid and an outer porous layer were fabricated by spark plasma sintering (SPS). When sintered at 750 degrees C, the NiTi alloy with 14% porosity in the inner part and 49% porosity as well as 350 mm average pore size in the outer layer exhibits an exceptionally high compressive strength (similar to 1375 MPa), together with an excellent superelastic recovery strain (>4%) and favorable cellular affinity (ROS1728 osteoblasts). Altogether, this work provides a strategy to design materials with function-structure integration and suggests that properly designed function-structure integrated NiTi alloys may be promising as advanced bone implants. (C) 2016 Elsevier Ltd. All rights reserved.