Solidification Behavior of Co-Sn Eutectic Alloy with Nb Addition

J. L. Kang,W. Xu,X. X. Wei,M. Ferry,J. F. Li
DOI: https://doi.org/10.1016/j.jallcom.2016.10.289
IF: 6.2
2016-01-01
Journal of Alloys and Compounds
Abstract:(Co76Sn24)(100-x)Nb-x (x = 0, 0.5, 0.8, 1.0) eutectic alloy melts were solidified at small undercooling for investigating the effect of Nb addition on microstructural development. With increasing Nb content, the solidification interface transits from eutectic seaweed (x = 0) to eutectic dendrite (x = 0.5) as a response to the change in the anisotropy of interfacial energy. Coupled eutectic growth can no longer be maintained within the main stems at x = 0.8 because the enrichment of Nb in the liquid ahead of the interface causes a significant difference in growth velocity between the alpha-Co and beta-Co3Sn2 phases and, as such, Co3Sn2 doublons form. For x = 1.0, the difference in growth kinetics between the two eutectic phases is so large that divorced eutectic growth takes place on a large scale. Letting the undercooling prior to solidification increase, the eutectic interface morphology of (Co76Sn24)(99.5)Nb-0.5 eutectic alloys returns from dendritic pattern back to factual seaweed pattern at more than 38 K undercooling and then transits to compact seaweed pattern at more than 181 K undercooling. The eutectic growth velocity slightly increases at low and intermediate undercooling but obviously decreases at large undercooling due with Nb addition. (C) 2016 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?