Intrinsic Polarization Switching in Batio3 Crystal under Uniaxial Electromechanical Loading

Yingwei Li,Jie Wang,Faxin Li

DOI: https://doi.org/10.1103/physrevb.94.184108

2016-01-01

Abstract:Both 180 degrees and 90 degrees intrinsic polarization switching (IPS) in BaTiO3 crystal were investigated by Landau-Ginzburg-Devonshire (LGD) theory under combined electric field and stress loading. Results show that for 180 degrees PS, the coercive electric field (E-IC(180)degrees) increases under tension but decreases under compression with increasing stresses. The 90 degrees PS was classified into two types. For type I 90 degrees PS, E-IC(I(90 degrees)) increases under tension but decreases under compression with increasing stresses, similar to 180 degrees PS; while for type II 90 degrees PS, an opposite variation trend is observed. (The definition of the type I and the type II 90 degrees PS is given in the text.) Additionally, the calculation demonstrates that under tensile stresses or under compressive stresses between -140 and 0 MPa, the electric field needed to drive both types of 90 degrees PS is smaller than that needed for driving 180 degrees PS, implying that 180 degrees PS is favorable to accomplish by two-step 90 degrees PS. As E-IC refers to 180 degrees PS in the past investigations, these demonstrate that the E-IC calculated by others may be overestimated. Moreover, the coercive stresses needed to drive 90 degrees ferroelastic IPS was also calculated as a function of preloading bias electric fields.