Role of Pd interlayer on NiTi to Ti6Al4V laser welded joints: microstructural evolution and strengthening mechanisms
Fissha Biruke Teshome,Bei Peng,J.P. Oliveira,Jiajia Shen,Sansan Ao,Haoyue Li,Caiwang Tan,Xiaoguo Song,Naixun Zhou,Zhi Zeng,Chen Long
DOI: https://doi.org/10.1016/j.matdes.2023.111845
2023-03-23
Abstract:Obtaining a reliable NiTi to Ti6Al4V dissimilar joint exhibiting NiTi's superelasticity can provide design flexibility in aerospace and biomedical fields via integrating distinct material benefits. However, this couple is vulnerable to severe embrittlement due to the development of excessive intermetallic compounds (IMCs), namely Ti 2 Ni. Pd-free and Pd-interlayered NiTi-Ti6Al4V laser joints were evaluated for their microstructure, compositional changes, thermodynamic mechanism, and mechanical properties. The presence of Pd constrained the formation of Ti 2 Ni IMC, and NiTi-Ti6Al4V joints with excellent mechanical properties demonstrating superelastic behavior were achieved for the first time. The tensile strength and rupture strain of the Pd-added NiTi-Ti6Al4V joint improved more than twofold, reaching 520 MPa and 5.6%, respectively. During cyclic tensile testing, the Pd-added joint demonstrated superelasticity and a comparable irrecoverable strain to NiTi (1 versus 0.65%). Multiscale characterization revealed that the fraction of Ti 2 Ni decreased from 83 to 10% near the NiTi boundary and 24 to 6% at the weld center compared to the Pd-free joint. The superior thermodynamic formation tendency of Ti-Pd compounds over Ti 2 Ni IMC favored their development, and thus Ti-Pd and NiTi compounds dominated the fusion zone (FZ) at the expense of Ti 2 Ni IMC, explaining the improved mechanical performance of the Pd-added joint.
materials science, multidisciplinary