Abstract:Traditional laser processing technique is mainly applied for cardiovascular stent manufacture, especially for materials with high mechanical properties and high melting point, while it usually produces problems such as material ablation and defects during finish machining process. Magnesium alloy, as material candidate for bioresorbable cardiovascular stent, has low melting and ignition point, high oxidizability property. Laser processing technique scarcely meets the requirements of high surface quality of magnesium alloy cardiovascular stents, this paper firstly develops a five-axis micro-milling technique to fabricate magnesium alloy cardiovascular stents. Milling orthogonal test was carried out to obtain the optimal finish machining parameters, and then a novel stent machining process was established. The processed stent has an inner diameter of 1.5 mm, a thickness of 80 & mu;m and a length of 8 mm with a U-bend width of 100 & mu;m and a link strut width of 70 & mu;m, and the optimal finish processing parameters was set up with the main spindle speed of 30,000 rpm, feed speed 200 mm/min, cutting width 50 & mu;m and cutting depth 40 & mu;m. The dimensional accuracy and surface topography of the magnesium alloy stent were measured and characterized, and results showed that the dimensional accuracy was within 0.01 mm, and the machined stent achieved better surface quality without obvious processing defects such as pits, grooves and pores while comparing with the stent under original processing parameters. In order to evaluate the radial support performance of the stent, the radial compression and expansion experiments and simulations were conducted, respectively. Results showed that the maximum diameter error in the experiment and simulation was 13.35 %, and the radial recoiling error was 16.79 %. This work provides a potential stent manufacture technique in the development and clinical application of bioresorbable magnesium alloy stent.

Preparation of the Micro/nano Structures of the Biomimetic Coating Stent for Loading MiRNA126 by Four-Beam Laser Interference

Experimental research on laser interference micro/nano fabrication of hydrophobic modification of stent surface

Fabrication of Hydrophobic Structures on Coronary Stent Surface Based on Direct Three-Beam Laser Interference Lithography

Multiple-drug Delivery from Mesoporous Coating Realizing Combination Therapy for Bare Metal Stents.

Micelle-Embedded Layer-by-Layer Coating with Catechol and Phenylboronic Acid for Tunable Drug Loading, Sustained Release, Mild Tissue Response, and Selective Cell Fate for Re-endothelialization.

High-Performance Self-Expanding NiTi Stents Manufactured by Laser Powder Bed Fusion

Exploring the potential of laser-textured metal alloys: Fine-tuning vascular cells responses through in vitro and ex vivo analysis

Fabricating hierarchical micro and nano structures on implantable Co-Cr-Mo alloy for tissue engineering by one-step laser ablation

Multilayer modification on titanium surface for in situ delivery of MicroRNAs

Coronary Stents Decorated by Heparin/NONOate Nanoparticles for Anticoagulant and Endothelialized Effects.

Interfacing exogenous stents with human coronary artery by self-assembled coating: designs, functionalities and applications

Bioinspired Vascular Stents with Microfluidic Electrospun Multilayer Coatings for Preventing in‐stent Restenosis

Design and Testing of Hydrophobic Core/hydrophilic Shell Nano/micro Particles for Drug-Eluting Stent Coating

Biomimetic Cardiovascular Stents for in Vivo Re-Endothelialization

Fabrication of a Novel Polymer-Free Nanostructured Drug-Eluting Coating for Cardiovascular Stents.

Multifunctional nanocoatings with synergistic controlled release of zinc ions and cytokines for precise modulation of vascular intimal reconstruction

Endothelium-Mimicking Multifunctional Coating Modified Cardiovascular Stents Via a Stepwise Metal-Catechol-(Amine) Surface Engineering Strategy

Study on Surface Quality and Mechanical Properties of Micro-Milling WE43 Magnesium Alloy Cardiovascular Stent

"Synergistic anticoagulant and endothelial regeneration strategy" based on mussel-inspired phospholipid copolymer coating and bioactive zeolitic imidazolate frameworks-90 to maintain the patency of CoCr stent

Design, preparation and performance of a novel drug-eluting stent with multiple layer coatings.

Immobilization of nano Cu-MOFs with polydopamine coating for adaptable gasotransmitter generation and copper ion delivery on cardiovascular stents