Increasing Energy Storage Capabilities of Space-Charge Dominated Ferroelectric Thin Films Using Interlayer Coupling

Hanfei Zhu,Menglin Liu,Yunxiang Zhang,Zhenghai Yu,Jun Ouyang,Wei Pan

DOI: https://doi.org/10.1016/j.actamat.2016.09.051

IF: 9.4

2016-01-01

Acta Materialia

Abstract:In our previous work (W. Zhang et al., Space-charge dominated epitaxial BaTiO3 heterostructures, Acta Mater. 85 (2015) 207-215), it was demonstrated that a space charge dominated BaTiO3 thin film can have much improved energy storage characteristics when compared with a regular insulating film of ferroelectric BaTiO3. However, the improved recoverable electric energy density (discharged energy per unit volume), W-re, is still constrained by the maximum/saturated polarization (P-s) of the BaTiO3 thin film. Here we propose a novel method to further improve W-re in ferroelectric thin film heterostructures by using interlayer coupling in an epitaxial ferroelectric bilayer. In our model structure, a ferroelectric BiFeO3 layer with a large remnant polarization (P-r similar to 70 mu C/cm(2)) was deposited in-situ on top of a BaTiO3/SrRuO3 heterostructure which shows a small remnant polarization (P-r similar to 3 mu C/cm(2)). The resulted bilayer structure showed a slim P-E hysteresis loop characterized by a small remnant polarization and a large saturated one (P-s >> P-r), which can be well explained by a competition between the effect of space charges (dominant at low field) and that of the interlayer charge coupling (dominant at high field). The large difference, i.e. P-s - P-r, increases the recoverable electric energy density by about 85% (from 28 J/cm(3) to 51 J/cm(3)). (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.