Abstract:In this work, a durable superhydrophobic fabric was fabricated by using a facile UV-induced surface covalent modification strategy. 2-isocyanatoethylmethacrylate (IEM) containing isocyanate groups can react with the pre-treated hydroxylated fabric, producing IEM molecules covalently grafted onto the fabric's surface, and the double bonds of IEM and dodecafluoroheptyl methacrylate (DFMA) underwent a photo-initiated coupling reaction under UV light radiation, resulting in the DFMA molecules further grafting onto the fabric's surface. The Fourier transform infrared, X-ray photoelectron spectroscopy and scanning electron microscopy results revealed that both IEM and DFMA were covalently grafted onto the fabric's surface. The formed rough structure and grafted low-surface-energy substance contributed to the excellent superhydrophobicity (water contact angle of ~162°) of the resultant modified fabric. Notably, such a superhydrophobic fabric can be used for efficient oil–water separation, for example a high separation efficiency of over 98%. More importantly, the modified fabric exhibited excellent durable superhydrophobicity in harsh conditions such as immersion in organic solvents for 72 h, an acidic or alkali solution (pH = 1–12) for 48 h, undergoing laundry washing for 3 h, exposure to extreme temperatures (from −196° to 120°), as well as damage such as 100 cycles of tape-peeling and a 100-cycle abrasion test; the water contact angle only slightly decreased from ~162° to 155°. This was attributed to the IEM and DFMA molecules grated onto the fabric through stable covalent interactions, which could be accomplished using the facile strategy, where the alcoholysis of isocyanate and the grafting of DFMA via click coupling chemistry were integrated into one-step. Therefore, this work provides a facile one-step surface modification strategy for preparing durable superhydrophobic fabric, which is promising for efficient oil–water separation.

Facile Process for the Fabrication of Durable Superhydrophobic Fabric with Oil/water Separation Property

Fabrication of a Novel Superhydrophobic and Superoleophilic Surface by One-Step Electrodeposition Method for Continuous Oil/water Separation

Transformation of Hydrophilic Cotton Fabrics into Superhydrophobic Surfaces for Oil/water Separation

Feasible Fabrication of A Durable Superhydrophobic Coating on Polyester Fabrics for Oil-Water Separation

Robust Superhydrophobic Fabric for Durability, Self‐Cleaning, and Oil/Water Separation Via Thiol–Acrylate Polymerization

Superhydrophobic Cotton Fabric Coated With Tannic Acid/Polyhedral Oligomeric Silsesquioxane For Highly Effective Oil/Water Separation

Facile preparation of cotton fabric modified with iron oxide nanoparticles with durable superhydrophobicity for oil/water separation

Fabrication of Durable Superhydrophobic Coating on Fabrics Surface for Oil/water Separation

A Facile Approach to Fabricate the Durable and Buoyant Superhydrophobic Fabric for Efficient Oil/Water Separation

A Durable Underwater Superoleophobic and Underoil Superhydrophobic Fabric for Versatile Oil/water Separation

Robust and Durable Superhydrophobic Cotton Fabrics for Oil/Water Separation

Facile UV-Induced Surface Covalent Modification to Fabricate Durable Superhydrophobic Fabric for Efficient Oil–Water Separation

Fabrication of Durable Superhydrophobic Surface for Versatile Oil/Water Separation Based on HDTMS Modified PPy/ZnO

Stable and Durable Superhydrophobic Cotton Fabrics Prepared via a Simple 1,4‐Conjugate Addition Reaction for Ultrahigh Efficient Oil‐Water Separation

Durable Superhydrophobic Cotton Fabrics Based on Fluorinated Alternating Copolymer and Silica Nanoparticle: Preparation and Oil-Water Separation

Design of fluorine-free superhydrophobic silk fabrics with mechanical durability and self-cleaning properties for oil-water separation

Fabrication of Durable Superhydrophobic and Superoleophilic Cotton Fabric with Fluorinated Silica Sol Via Sol-Gel Process

Fabrication of Superhydrophobic and Superoleophilic Textiles for Oil–water Separation

Vapor-Liquid Sol-Gel Approach to Fabricating Highly Durable and Robust Superhydrophobic Polydimethylsiloxane@Silica Surface on Polyester Textile for Oil-Water Separation

Durable and Recyclable Superhydrophilic-Superoleophobic Materials for Efficient Oil/Water Separation and Water-Soluble Dyes Removal

Two-Step Approach for Fabrication of Durable Superamphiphobic Fabrics for Self-Cleaning, Antifouling, and On-Demand Oil/Water Separation