A Dft Study of Mechanical Properties, Thermal Conductivity and Electronic Structures of Th-Doped Gd2zr2o7

F. A. Zhao,H. Y. Xiao,Z. J. Liu,Sean Li,X. T. Zu

DOI: https://doi.org/10.1016/j.actamat.2016.09.018

IF: 9.4

2016-01-01

Acta Materialia

Abstract:A systematic density functional theory study is performed to investigate the mechanical stability, elastic moduli, Debye temperature, thermal conductivity and electronic structures of Gd2-yThyZr2O7 and Gd2Zr2-yThyO7. All the Th-doped Gd2Zr2O7 compositions are found to be structurally and mechanically stable. As compared with the pure Gd2Zr2O7, Th incorporation into both Gd-site and Zr-site results in generally better ductility, lower Debye temperature, and reduced thermal conductivity. The reduction in thermal conductivity can be as high as 25–32%, depending on the content of the Th substituent. Our calculations suggest that Th-doped Gd2Zr2O7, especially Gd2Zr2-yThyO7, exhibits better mechanical and thermal properties that are beneficial to its application as thermal barrier coating material at high temperatures than the pure state.