Abstract:Bisphenol A dicyanate ester resins modified by fluorine-containing liquid crystal compound (LCFE) are applied as polymer matrix (LCFE-BADCy), poly( p-phenylene-2,6-benzobisoxazole) (PBO) fibers as rein-forcements, and fluorine/adamantane PBO precursor (preFABPBO) as interfacial compatibilizer to prepare the corresponding PBO fibers/FABPBO/LCFE-BADCy wave-transparent laminated composites. LCFE could improve the order degree of BADCy cured network, in favor of enhancing the wave-transparent perfor-mance, mechanical properties, and intrinsic thermal conductivity. The dielectric constant and dielectric loss of PBO fibers/FABPBO/LCFE-BADCy composites are highly temperature (25-200 degrees C) and frequency (10 4 -10 7 Hz and 8.2-12.4 GHz) stable with the value of 2.49 and 0.003 under 10 6 Hz at 25 degrees C, and the corresponding wave transmission efficiency is 95.0%, higher than that of 92.5% for PBO fibers/BADCy com-posites. The interlamellar shear strength and flexural strength are respectively 50.7 MPa and 682.5 MPa, 38.1% and 16.2% higher than those of PBO fibers/BADCy composites. Besides, the volume resistivity, breakdown voltage, heat resistance index, glass transition temperature, flame retardant grade, and ul-timate oxygen index of PBO fibers/FABPBO/LCFE-BADCy composites are respectively 5.3 x 10 15 Q cm, 29.75 kV/mm, 217.2 degrees C, 245.7 degrees C, V-1 grade, and 33.6%, expected to be performed as a new generation of "lightweight/loading/wave-transparent" electromagnetic window materials in advanced military weapons and civil communication base station.(c) 2023 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Atomic Oxygen Erosion Behaviors of Pbo Fibers and Their Composite: Microstructure, Surface Chemistry and Physical Properties

Grafting of Silane and Graphene Oxide Onto PBO Fibers: Multifunctional Interphase for Fiber/polymer Matrix Composites with Simultaneously Improved Interfacial and Atomic Oxygen Resistant Properties

Surface modification of PBO fibers by direct fluorination and corresponding chemical reaction mechanism

PBO fibers/fluorine-containing liquid crystal compound modified cyanate ester wave-transparent laminated composites with excellent mechanical and flame retardance properties

Facile preparation of ultraviolet resistant “hard armors” on poly(p-phenylene benzobisoxazole) fibers through heat-induced surface treatment

Atomic Oxygen-Induced Surface Erosion Behavior and Mechanical Degradation of Polyether Ether Ketone Via Reactive Molecular Dynamics Simulations

Surface modification of PBO fiber through oxygen plasma induced vapor phase grafting of acrylic acid

Study on Photoaging of Poly(p‐phenylene Benzobisoxazole) Fiber

Study on the Photolysis and Stabilization of PBO Fiber

AO-resistant Properties of Polyimide Fibers Containing Phosphorous Groups in Main Chains

Processing and characterization of ZnO nanowire-grown PBO fibers with simultaneously enhanced interfacial and atomic oxygen resistance properties

Branched Fluorine/Adamantane Interfacial Compatibilizer for PBO Fibers/Cyanate Ester Wave-Transparent Laminated Composites

A reactive molecular dynamics simulation of the atomic oxygen impact on poly(p-phenylene-terephthalamide)

Synthesis and AO Resistant Properties of Novel Polyimide Fibers Containing Phenylphosphine Oxide Groups in Main Chain

Atomic oxygen effects on polymers containing silicon or phosphorus: Mass loss, erosion yield, and surface morphology

Uv Aging Resistance Properties of Pbo Fiber Coated with Nano-Zno Hybrid Sizing

Synthesis and Properties of Poly[P-(2,5-Dihydroxy)-Phenylenebenzobisoxazole] Fiber

Aging and protection of PBO fiber

Experimental Study of Basic Properties of PBO Organic Fibe r

Enhanced UV Stability of PBO Fibers by Using Benzotriazole UV Absorber

Photostabilisation of Poly(P-Phenylenebenzobisoxazole) Fibre