Influence of Solution Chemistry on the Dielectric Properties of TiO2 Thin-Film Porous Electrodes

Yang Wang,M. Isabel Tejedor-Tejedor,Wei Tan,Marc A. Anderson

DOI: https://doi.org/10.1021/acs.jpcc.6b07061

2016-01-01

The Journal of Physical Chemistry C

Abstract:The development of supercapacitors having enhanced energy is of technological importance. Since energy scales not only with the square of the voltage but also with capacitance, we have focused on the role of the dielectric constant in enhancing capacitance. TiO2 thin-films were deposited on Si wafers by dip-coating techniques. The inhomogeneity of TiO2 thin-film generated by dip-coating and changes in crystal structure with different firing temperature were shown to be important variables in this system. Using ellipsometry under controlled humidity, we were able to measure the refractive index of pore water. Surprisingly, the refractive index of pore water decreases with increasing ionic strength, which is the opposite case of bulk water as measured by the ellipsometer. Furthermore, we found that the surface potential also influences the refractive index of pore water. Electrophoretic mobility studies were used to show the role of surface potential at the pore wall influencing the properties of yore water. The higher the surface potential, the higher the refractive index, the lowest refractive index occurring dose to the isoelectric pH. The presence of the specifically adsorbed phosphate ions on the pore walls increases the refractive index. Electrochemical charge-discharge measurements were performed using TiO2 thin-films coated on platinized Ti Coupons to obtain the capacitance of these TiO2 thin-film systems. The capacitance followed, a similar trend as are zeta potential and can be improved by phosphate addition. It should be noted that refractive indices that We have obtained from measurements using the,ellipsometer only qualitatively relate to capacitance since they were acquired at much higher frequency than those we normally used to measure capacitance. However, the combined value of these experiments should help add insight into the nature of structured water and fundamental electrochemistry inside biased nanoporous oxide thin-films.