Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Hydrothermal Synthesis of Nanosized ZSM-22 and Their Use in the Catalytic Conversion of Methanol

Synthesis of ZSM-22 Zeolite Nanosheets with Improved Stability in the Catalytic Conversion of Methanol to Hydrocarbons

Size controllable synthesis of ZSM-5 zeolite and its catalytic performance in the reaction of methanol conversion to aromatics

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Thermostability of Nanosized HZSM-5 Zeolite

The Preparation Of Nano-Sized Cu-Zsm-5 Zeolite And Its Catalytic Performance

Green synthesis of shaped nano-ZSM-5 toward more efficient methanol-to-hydrocarbon conversion

Facile synthesis of ultrafine nanosized ZSM-5 zeolite using a hydroxyl radical initiator for enhanced catalytic performance in the MTG reaction

Effect of Hierarchical ZSM-5 Zeolite Crystal Size on Diffusion and Catalytic Performance of N-Heptane Cracking

Preparation of nano ZSM-5 with hydrophobic surfaces and application to catalytic cracking of hydrocarbon fuels

Effect of the Si/Al Ratios of Nanocrystalline HZSM-5 Zeolite on the Performance in Catalytic Conversion of Ethanol to Propylene

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

One-step Synthesis of Hierarchical ZSM-5 Zeolites and Their Catalytic Performance on the Conversion of Methanol to Aromatics

Catalytic Study of Methanol-to-Propylene Conversion over Nano-Sized HZSM-5

Synthesis of nanosheet SSZ-39 zeolite with enhanced catalytic performance in methanol-to-olefins reaction

Influence of framework Al distribution in HZSM-5 channels on catalytic performance in the methanol to propylene reaction

Atmospheric Pressure Synthesis Of Nanosized Zsm-5 With Enhanced Catalytic Performance For Methanol To Aromatics Reaction

Catalytic Performance of Methanol to Aromatics over Hierarchical ZSM-5 Zeolite Synthesized by a Soft Template Method

Effect of crystal size of ZSM-11 zeolite on the catalytic performance and reaction route in methanol to olefins

Co-conversion of Methanol and N -Hexane into Aromatics Using Intergrown ZSM-5/ZSM-11 As a Catalyst

Modification of ZSM-23 zeolite via vapor-phase transport method: reducing the length along the unidimensional channels for enhanced catalytic performances in methanol-to-hydrocarbons