Abstract:Si 3 N 4 ceramic was jointed to itself using (CuZn)85Ti15 filler alloy at 1123-1323 K for 0.9 ks. TEM observation showed that a reaction zone of TiN and/or Ti 2 N exists at the interface between the ceramic and filler alloy. When the brazing temperature is lower than 1223 K, the interfacial reaction zone is mainly composed of Ti 2 N, which has cylindrical shape and is randomly orientate in the zone. There is a crystal orientation relationship between the Ti 2 N in the reaction zone and the Cu in the Cu-Zn solid solution, which is: {110} n 2 N // {420} C u , T i 2 N // C u . When the brazing temperature is higher than 1223 K, the interfacial zone is composed of TiN, which has plate shapes crossing each other.

Interfacial microstructure and reaction phases in Si3N4/Si3N4 joints brazed with Cu-Zn-Ti filler alloy