Abstract:A series of Ce-modified Cu-FeOx catalysts were synthesized with a sol-gel hydrothermal method. These catalysts contained different molar ratios of Ce, Cu, and Fe, and were applied to the process of NO catalytic removal by CO (CO-deNO). The physical and chemical parameters of the samples were characterized by XRD, XPS, ESR, H-2-TPR, NO-TPO, and NO-TPD techniques. Moreover, the CO-deNO mechanisms for the representative catalysts were investigated by in situ DRIFTS. The SO2 and H2O resistances, and their corresponding mechanisms, were also systematically investigated. The catalytic activity testing shows that the optimized molar ratio of Cu, Ce, and Fe is 1:0.5:1.5. At this ratio, the CO-deNO efficiency is highest, but the N2O selectivity is also relatively high. Increasing the Fe percentage could reduce the N2O concentration. The characterization indicates that, at the optimized ratio, the interaction between Fe and Cu is at its strongest, which could increase the formation probability of surface synergistic oxygen vacancies. The Ce existing in the catalysts plays a key role in the adsorption of NO and CO. Moreover, the increasing percentage of Fe could enhance the adsorption and dissociation of NO, and promote the evolution of CO, which can compensate for the effects of the weaker interaction. The NO and CO evolution pathway runs as follows: NO -> M-NO2 -> NO2- -> M-N2O/NO3- -> N2O/N-2; CO -> COO- -> CO32- -> CO2. The H2O and SO2 resistance tests suggest that the appropriate incremental increase in Fe percentage will increase the SO2 or H2O resistance, with the underlying mechanism being that Fe inhibits the formation of sulfates and produces more water adsorption sites, and the increasing Fe percentage would optimize the pore structure.

A CeFeOx Catalyst for Catalytic Oxidation of NO to NO2

FeCeOx with Improved Activity for Catalytic Reduction of NO with NH3

Low-temperature catalytic oxidation of NO over Mn-Ce-Ox catalyst

Reaction of NO + CO over Ce-Modified Cu–FeOx Catalysts at Low Temperature

The Inter-Connected Porous CuOx-NbOx/kit-CeO2 Catalyst:Enhanced Activity, Resistance of SO2 and H2O for the Removal of NOx

Constructing Efficient CuO -Ceo2 Catalyst for NO Reduction by CO: New Insights into the Structure–activity Relationship

Low temperature selective catalytic reduction of NO with NH3 over CeFeOx catalyst

Promotional Effect of N-doped CeO2 Supported CoOx Catalysts with Enhanced Catalytic Activity on NO Oxidation

Low-temperature Catalytic Oxidation of NO over Mn–Co–Ce–Ox Catalyst

Role and Reduction of NOx in the Catalytic Combustion of Soot over Iron–ceria Mixed Oxide Catalyst

Investigation of intrinsic catalytic mechanism for NO oxidation to NO<sub>2</sub> in CeO<sub>2</sub> used for NO removal

Synergetic Effects of Surface Free Co3O4 Species on Catalytic Oxidation of NO over Cerium-Cobalt Solid Solution

Nickel foam supported CuCe mixed metal oxide as monolith catalyst for NO removal

Ce(SO4)2/α-Fe2O3 selective catalytic reduction of NOx with NH3: preparation, characterization, and performance

Promoting Mechanism of CuO on Catalytic Performance of CeFe Catalyst for Simultaneous Removal of NOx and CO

Preparation and Investigation of Iron–Cerium Oxide Compounds for NOx Reduction

Insight into the Mesoporous Fe Ce1−O2− Catalysts for Selective Catalytic Reduction of NO with NH3: Regulable Structure and Activity

Preparation and characterization of CeO<sub>2</sub>–Fe<sub>2</sub>O<sub>3</sub> catalysts for the selective catalytic reduction of NO with CO

Selective catalytic oxidation of NO with O2 over Ce-doped MnOx/TiO2 catalysts

Single-Atom Ce-Modified Α-Fe2o3 for Selective Catalytic Reduction of NO with NH3.

Understanding Structure-Performance Relationships of CoOx/CeO2 Catalysts for NO Catalytic Oxidation: Facet Tailoring and Bimetallic Interface Designing.