Evaluation of Shear Moduli and Other Properties of Silicates with the Spinel Structure from Ir Spectroscopy

AM Hofmeister,HK Mao

DOI: https://doi.org/10.2138/am-2001-5-604

IF: 3.066

2001-01-01

American Mineralogist

Abstract:Vibrational spectra are used to determine key physical properties of phases thought to be important in Earth's transition zone. Single-crystal infrared (IR) reflectance spectra were measured for synthetic Mg, Fe, Ni, or Go-bearing silicates with the spinel structure. Peak parameters (frequency, damping coefficient, and oscillator strength) were determined for the fundamentals, and for overtones, up to 3(rd) order. On average, the frequencies and damping coefficients of the overtones are simple multiples of the corresponding parameters of the fundamental modes. Absorption spectra of thin films were measured at pressures (P) up to 370 kbar for gamma -Mg2SiO4 and up to 200 kbar for gamma -Fe2SiO4. Widths are nearly constant, but frequencies (vi) increase either linearly or quadratically with P, For weak peaks. the absorption widths have values close to their corresponding damping coefficients. For gamma -Fe2SiO4, ambient IR data predict heat capacity (C-v = 126 +/- 2.5 J/mol.K), shear modulus (G = 875 +/- 15 kbar), and sound velocities (u(p) = 8.20 +/- 0.05, u(s) = 4.25 +/- 0.06 km/s) at 298 K: pressure data give partial derivativeG/partial derivativeP = 0.06, 0.44, or 0.91 if for the bulk modulus, partial derivativeK/partial derivativeP = 5, 4.5, or 4, respectively, and an average mode Gruneisen parameter of < gamma > = 1.45 +/- 0.4, which implies that thermal expansivity is (21 +/- 1) x 10(-6)/K. For gamma -Mg1.2Fe0.8SiO4, ambient IR data predict G = 1120 +/- 50 kbar, U-p = 9.12 +/- 0.20, and u(s) = 5.18 +/- 0.20 km/s at 298 K, assuming that the frequency of the acoustic mode is 225 to 240 cm(-1). This calculation uses K-s = 1995 kbar, which was obtained from recent compression data by assuming partial derivativeK/partial derivativeP = 4. The above values provide a smooth quadratic dependence of K, and G on Fe/(Fe + Mg). The trends suggest that partial derivativeK/partial derivativeP remains at 4 whereas partial derivativeG/partial derivativeP drops from similar to1 to similar to0.5 as Fe content increases in ringwoodite. Acoustic fundamentals or overtones were used successfully here to provide u, G, and their P and T derivatives for silicate spinels. This method should work for other simple structures, and may be generally applicable.