Cobalt-based Metal Organic Framework with Superior Lithium Anodic Performance

Xiaoshi Hu,Huiping Hu,Chao Li,Tian Li,Xiaobing Lou,Qun Chen,Bingwen Hu
DOI: https://doi.org/10.1016/j.jssc.2016.07.021
IF: 3.3
2016-01-01
Journal of Solid State Chemistry
Abstract:The reversible charging of a Co-1,4-benzenedicarboxylate MOF (Co-BDC MOF) prepared via an one-pot solvothermal method was studied for use as the anode in a Li-ion cell. It was found that this MOF anode provides high reversible capacities (1090 and 611mAhg−1 at current densities of 0.2 and 1Ag−1, respectively), and an impressive rate performance. Such an outstanding Li-ion storage property has not been reported previously for the LIB anodes within the MOFs category. Ex-situ X-ray photoelectron spectroscopy (XPS) and infrared spectroscopy (IR) studies of this material at different state of charge suggest that cobalt stays at Co2+ state during discharge/charge process, so that in this case Li+ may be inserted into the organic moiety without the direct participation of cobalt ions.
What problem does this paper attempt to address?