SiO2-g-PS/fluoroalkylsilane Composites for Superhydrophobic and Highly Oleophobic Coatings

Liang Junyan,Wang Li,Bao Jingxian,He Ling

DOI: https://doi.org/10.1016/j.colsurfa.2016.07.056

IF: 5.518

2016-01-01

Colloids and Surfaces A Physicochemical and Engineering Aspects

Abstract:Alkenyl-functionalized SiO2 particles (AFSPs) were prepared, grafted and co-cast with fluoroalkylsilane to produce superhydrophobic and highly oleophobic coatings. In preparation of AFSPs, vinyltrimethoxysilane (VTMS) and gamma-methacryloxypropyltrimethoxysilane (MPTMS) were employed separately to react with SiO2 nanoparticles (NPs) through the ex situ neutral condensation. In contrast, the reaction of MPTMS with SiO2 NPs was also executed through the in situ alkali-catalyzed sol-gel technique. It showed that the obtained neutral condensed VTMS-SiO2 and MPTMS-SiO2 NPs had a surface with a thin grafted layer of VTMS and MPTMS, respectively, whereas the alkali-catalyzed MPTMS-SiO2 NPs had a surface bearing a slightly thicker MPTMS hydrolysate-condensate layer. Polystyrene (PS) was allowed to graft onto the AFSPs to prepare SiO2-g-PS particles via emulsion polymerization of styrene (St) from each of these three AFSPs. The uniform SiO2-g-PS particles were obtained exclusively by the growth of PS from neutral condensed MPTMS-SiO2 NPs. SiO2-g-PS/fluoroalkylsilane composites for coating were subsequently prepared by the in situ hydrolysis of 1H, 1H, 2H, 2H-perfluorodecyltriethoxysilane (FDTES) in the suspension of uniform SiO2-g-PS particles. It was found that the use of smaller SiO2-g-PS particles and high-content FDTES contributed to the creation of a coating that exhibited superhydrophobicity with low adhesion and high oleophobicity with high adhesion. (C) 2016 Elsevier B.V. All rights reserved.