Abstract:High-efficiency supersonic atmospheric plasma spraying was used to fabricate Ni-C and NiCrAl-BN abradable seal coatings. The erosion wear, corrosion resistance and wear resistance of plasma-sprayed coatings were comparatively studied. Experimental results showed that the libricating phases were homogeneously distributed in the as-sprayed coatings while their average size of the coating was much fine compared with Ni-C coating, and the former also showed higher surface hardness than the latter. Meanwhile, it was found that the erosive mass loss increased with the increase of impingement angle from 30 degrees to 90 degrees and the relative erosion rate of NiCrAl-BN coating was only a half of that of Ni-C coating. Due to the formation of corrosion product around the flake graphite, the corrosion resistance of NiCrAl-BN coating was better than Ni-C coating in dilute hydrochloric acid (1vol%). However, the hydrochloric acid could permeate the NiCrAl-BN coating through the pores, which resulted in the localized corrosion of metal phases. In addition, we also observed that the friction coefficient of NiCrAl-BN coating significantly decreased from room temperature to 400 degrees owing to the formation of large-scale self-lubricating film that resulted from the improvement of plasticity and fluidity of BN.

Corrosion Resistance and Anti-Wear Property of Nickel Based Abradable Sealing Coating Deposited by Plasma Spraying